A study on the design method for the material composition of small particle-size asphalt mixture for controlling cracks in asphalt pavement

Jiyu Xin, Jianzhong Pei, Mitsuyoshi Akiyama, Rui Li, Jiupeng Zhang, Libo Shao

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

Generally, various kinds of cracks are the main type of distresses during the service period of asphalt pavements. To save maintenance costs and improve the crack resistance of asphalt pavements effectively, this paper presents a unique design method for the material composition of small particle-size (SPS) asphalt mixture for controlling cracks in asphalt pavement. First, Stone Mastic Asphalt (SMA)-II was designed as a basic gradation according to the A.N. Talbot curve and SMA-II-1, SMA-II-2 and SMA-II-3 were designed according to the Superpave mix design method, the Bailey method and the Particle interference theory, respectively. Second, based on Marshall test results, the optimal fiber content and optimal asphalt content of three gradations were determined. Then, the influence of the passing rate of 1.18-mm sieve and 0.075-mm sieve on the air voids of SMA-II and the influence of the filler-asphalt ratio on the performance of SMA-II were investigated, and an appropriate range of filler-asphalt ratio was obtained. Finally, a high-temperature performance test, a water stability test, and a skid resistance test demonstrate that the overall performance of SMA-II can satisfy the specifications. A low-temperature bend test and analysis of bending strain energy density show that SMA-II with a crumb rubber modifier and a polymer fiber has better crack resistance performance than SMA-I (SBS-modified mixture). Life-cycle cost analysis shows the economic advantage of SPS asphalt thin overlays over traditional AC-13 thin overlays.

Original languageEnglish
Article number1988
JournalApplied Sciences (Switzerland)
Volume9
Issue number10
DOIs
Publication statusPublished - 2019 May 1

Fingerprint

Mastic asphalt
asphalt
pavements
Asphalt mixtures
Asphalt pavements
cracks
Particle size
Cracks
Chemical analysis
Asphalt
rocks
Pavement overlays
Sieves
Fillers
Superpave
Skid resistance
sieves
mastic asphalt
Fibers
Rubber

Keywords

  • Cracks control
  • Crumb rubber modifier
  • Life-cycle cost analysis
  • Material composition
  • Pavement performance test
  • Polyester fiber
  • Small particle-size (SPS) asphalt mixture

ASJC Scopus subject areas

  • Materials Science(all)
  • Instrumentation
  • Engineering(all)
  • Process Chemistry and Technology
  • Computer Science Applications
  • Fluid Flow and Transfer Processes

Cite this

A study on the design method for the material composition of small particle-size asphalt mixture for controlling cracks in asphalt pavement. / Xin, Jiyu; Pei, Jianzhong; Akiyama, Mitsuyoshi; Li, Rui; Zhang, Jiupeng; Shao, Libo.

In: Applied Sciences (Switzerland), Vol. 9, No. 10, 1988, 01.05.2019.

Research output: Contribution to journalArticle

@article{3fef2f886baf4fcb84c2cd477576fc86,
title = "A study on the design method for the material composition of small particle-size asphalt mixture for controlling cracks in asphalt pavement",
abstract = "Generally, various kinds of cracks are the main type of distresses during the service period of asphalt pavements. To save maintenance costs and improve the crack resistance of asphalt pavements effectively, this paper presents a unique design method for the material composition of small particle-size (SPS) asphalt mixture for controlling cracks in asphalt pavement. First, Stone Mastic Asphalt (SMA)-II was designed as a basic gradation according to the A.N. Talbot curve and SMA-II-1, SMA-II-2 and SMA-II-3 were designed according to the Superpave mix design method, the Bailey method and the Particle interference theory, respectively. Second, based on Marshall test results, the optimal fiber content and optimal asphalt content of three gradations were determined. Then, the influence of the passing rate of 1.18-mm sieve and 0.075-mm sieve on the air voids of SMA-II and the influence of the filler-asphalt ratio on the performance of SMA-II were investigated, and an appropriate range of filler-asphalt ratio was obtained. Finally, a high-temperature performance test, a water stability test, and a skid resistance test demonstrate that the overall performance of SMA-II can satisfy the specifications. A low-temperature bend test and analysis of bending strain energy density show that SMA-II with a crumb rubber modifier and a polymer fiber has better crack resistance performance than SMA-I (SBS-modified mixture). Life-cycle cost analysis shows the economic advantage of SPS asphalt thin overlays over traditional AC-13 thin overlays.",
keywords = "Cracks control, Crumb rubber modifier, Life-cycle cost analysis, Material composition, Pavement performance test, Polyester fiber, Small particle-size (SPS) asphalt mixture",
author = "Jiyu Xin and Jianzhong Pei and Mitsuyoshi Akiyama and Rui Li and Jiupeng Zhang and Libo Shao",
year = "2019",
month = "5",
day = "1",
doi = "10.3390/app9101988",
language = "English",
volume = "9",
journal = "Applied Sciences (Switzerland)",
issn = "2076-3417",
publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",
number = "10",

}

TY - JOUR

T1 - A study on the design method for the material composition of small particle-size asphalt mixture for controlling cracks in asphalt pavement

AU - Xin, Jiyu

AU - Pei, Jianzhong

AU - Akiyama, Mitsuyoshi

AU - Li, Rui

AU - Zhang, Jiupeng

AU - Shao, Libo

PY - 2019/5/1

Y1 - 2019/5/1

N2 - Generally, various kinds of cracks are the main type of distresses during the service period of asphalt pavements. To save maintenance costs and improve the crack resistance of asphalt pavements effectively, this paper presents a unique design method for the material composition of small particle-size (SPS) asphalt mixture for controlling cracks in asphalt pavement. First, Stone Mastic Asphalt (SMA)-II was designed as a basic gradation according to the A.N. Talbot curve and SMA-II-1, SMA-II-2 and SMA-II-3 were designed according to the Superpave mix design method, the Bailey method and the Particle interference theory, respectively. Second, based on Marshall test results, the optimal fiber content and optimal asphalt content of three gradations were determined. Then, the influence of the passing rate of 1.18-mm sieve and 0.075-mm sieve on the air voids of SMA-II and the influence of the filler-asphalt ratio on the performance of SMA-II were investigated, and an appropriate range of filler-asphalt ratio was obtained. Finally, a high-temperature performance test, a water stability test, and a skid resistance test demonstrate that the overall performance of SMA-II can satisfy the specifications. A low-temperature bend test and analysis of bending strain energy density show that SMA-II with a crumb rubber modifier and a polymer fiber has better crack resistance performance than SMA-I (SBS-modified mixture). Life-cycle cost analysis shows the economic advantage of SPS asphalt thin overlays over traditional AC-13 thin overlays.

AB - Generally, various kinds of cracks are the main type of distresses during the service period of asphalt pavements. To save maintenance costs and improve the crack resistance of asphalt pavements effectively, this paper presents a unique design method for the material composition of small particle-size (SPS) asphalt mixture for controlling cracks in asphalt pavement. First, Stone Mastic Asphalt (SMA)-II was designed as a basic gradation according to the A.N. Talbot curve and SMA-II-1, SMA-II-2 and SMA-II-3 were designed according to the Superpave mix design method, the Bailey method and the Particle interference theory, respectively. Second, based on Marshall test results, the optimal fiber content and optimal asphalt content of three gradations were determined. Then, the influence of the passing rate of 1.18-mm sieve and 0.075-mm sieve on the air voids of SMA-II and the influence of the filler-asphalt ratio on the performance of SMA-II were investigated, and an appropriate range of filler-asphalt ratio was obtained. Finally, a high-temperature performance test, a water stability test, and a skid resistance test demonstrate that the overall performance of SMA-II can satisfy the specifications. A low-temperature bend test and analysis of bending strain energy density show that SMA-II with a crumb rubber modifier and a polymer fiber has better crack resistance performance than SMA-I (SBS-modified mixture). Life-cycle cost analysis shows the economic advantage of SPS asphalt thin overlays over traditional AC-13 thin overlays.

KW - Cracks control

KW - Crumb rubber modifier

KW - Life-cycle cost analysis

KW - Material composition

KW - Pavement performance test

KW - Polyester fiber

KW - Small particle-size (SPS) asphalt mixture

UR - http://www.scopus.com/inward/record.url?scp=85066490480&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85066490480&partnerID=8YFLogxK

U2 - 10.3390/app9101988

DO - 10.3390/app9101988

M3 - Article

VL - 9

JO - Applied Sciences (Switzerland)

JF - Applied Sciences (Switzerland)

SN - 2076-3417

IS - 10

M1 - 1988

ER -