Abstract
A single-roll caster and two kinds of twin-roll casters to cast clad strips were designed and assembled. One of twin-roll casters was suitable for clad strip casting. This twin-roll caster can cast clad strips of aluminum alloys at the speed of 20m/min. The thickness of the clad strip is about 2.0mm. The clad strip has a clear interface between the two strips. The clad strip is connected strongly at the interface. Therefore, the clad strip does not peel off at the interface after bending until broken. The clad ratio of the thickness between the overlay strip and the base strip is 2:1-1:10. An alloy with a melting point lower than that of the base strip is suitable for the overlay strip. The roll speed, cooling distance of the base strip, and the temperatures of the melt for the overlay strip are important factors in producing sound clad strips.
| Original language | English |
|---|---|
| Pages (from-to) | 366-371 |
| Number of pages | 6 |
| Journal | Journal of Materials Processing Technology |
| Volume | 138 |
| Issue number | 1-3 |
| DOIs | |
| Publication status | Published - 2003 Jul 20 |
| Externally published | Yes |
Fingerprint
Keywords
- Melt drag twin-roll caster
- Roll casting
- Strip casting
- Thin strip
- Twin-roll caster
ASJC Scopus subject areas
- Materials Science(all)
Cite this
A twin-roll caster to cast clad strip. / Haga, T.; Suzuki, Shinsuke.
In: Journal of Materials Processing Technology, Vol. 138, No. 1-3, 20.07.2003, p. 366-371.Research output: Contribution to journal › Article
}
TY - JOUR
T1 - A twin-roll caster to cast clad strip
AU - Haga, T.
AU - Suzuki, Shinsuke
PY - 2003/7/20
Y1 - 2003/7/20
N2 - A single-roll caster and two kinds of twin-roll casters to cast clad strips were designed and assembled. One of twin-roll casters was suitable for clad strip casting. This twin-roll caster can cast clad strips of aluminum alloys at the speed of 20m/min. The thickness of the clad strip is about 2.0mm. The clad strip has a clear interface between the two strips. The clad strip is connected strongly at the interface. Therefore, the clad strip does not peel off at the interface after bending until broken. The clad ratio of the thickness between the overlay strip and the base strip is 2:1-1:10. An alloy with a melting point lower than that of the base strip is suitable for the overlay strip. The roll speed, cooling distance of the base strip, and the temperatures of the melt for the overlay strip are important factors in producing sound clad strips.
AB - A single-roll caster and two kinds of twin-roll casters to cast clad strips were designed and assembled. One of twin-roll casters was suitable for clad strip casting. This twin-roll caster can cast clad strips of aluminum alloys at the speed of 20m/min. The thickness of the clad strip is about 2.0mm. The clad strip has a clear interface between the two strips. The clad strip is connected strongly at the interface. Therefore, the clad strip does not peel off at the interface after bending until broken. The clad ratio of the thickness between the overlay strip and the base strip is 2:1-1:10. An alloy with a melting point lower than that of the base strip is suitable for the overlay strip. The roll speed, cooling distance of the base strip, and the temperatures of the melt for the overlay strip are important factors in producing sound clad strips.
KW - Melt drag twin-roll caster
KW - Roll casting
KW - Strip casting
KW - Thin strip
KW - Twin-roll caster
UR - http://www.scopus.com/inward/record.url?scp=0038819052&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0038819052&partnerID=8YFLogxK
U2 - 10.1016/S0924-0136(03)00100-6
DO - 10.1016/S0924-0136(03)00100-6
M3 - Article
VL - 138
SP - 366
EP - 371
JO - Journal of Materials Processing Technology
JF - Journal of Materials Processing Technology
SN - 0924-0136
IS - 1-3
ER -