Cavitation failure in a superplastic alumina with zirconia-particle dispersion

K. Hiraga, Y. Sakka, T. S. Suzuki, K. Nakano

Research output: Contribution to journalConference article

5 Citations (Scopus)

Abstract

High temperature tensile in a fine-grained alumina with zirconia particle dispersion is found to relate closely to the separation distance among micrometer-sized cavities growing from preexistent defects and from newly formed ones during deformation. As the separation distance is decreased to a certain level with an increase in both density and size of such cavities, extensive cavity interlinkage starts to cause microcracking, and the microcracking leads to the occurrence of macroscopic cracks propagating in a direction perpendicular to the tensile axis toward the final failure. The dependence of the onset strain of microcracking on temperature and grain size is also found to relate closely to the dependence of cavity formation and growth rates on these factors.

Original languageEnglish
Pages (from-to)763-770
Number of pages8
JournalKey Engineering Materials
Volume171-174
Publication statusPublished - 2000 Jan 1
EventProceedings of the 1999 8th International Conference on Creep and Fracture of Engineering Materials and Structures - Tsukuba, Jpn
Duration: 1999 Nov 11999 Nov 5

    Fingerprint

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Hiraga, K., Sakka, Y., Suzuki, T. S., & Nakano, K. (2000). Cavitation failure in a superplastic alumina with zirconia-particle dispersion. Key Engineering Materials, 171-174, 763-770.