Cubic InGaN/GaN double-heterostructure light emitting diodes grown on GaAs (001) substrates by MOVPE

Y. Taniyasu, K. Suzuki, D. H. Lim, A. W. Jia, M. Shimotomai, Y. Kato, M. Kobayashi, A. Yoshikawa, K. Takahashi

Research output: Contribution to journalConference article

25 Citations (Scopus)

Abstract

Cubic (zinc-blende) InGaN/GaN double-heterostructure LEDs were fabricated on GaAs (001) substrates. The device performance and crystal quality were investigated. The emission wavelength was controlled by the In content in the cubic InGaN active layer. The violet-blue electroluminescence was observed around 435 nm with a FWHM of 55 nm from a cubic In0.07Ga0.93N/GaN DH LED. The forward voltage was 4.9 V at 20 mA and the reverse leakage current was 5 mA at -10 V. X-ray reciprocal space mapping measurement was performed to investigate the phase purity and strain in InGaN/GaN heterostructure. The mixing of the stable hexagonal phase in the cubic GaN was observed and the hexagonal phase content was about 10%. In-situ spectroscopic ellipsometry measurement showed that most of the mixed hexagonal domains were likely to be formed in the Mg-doped GaN layer. In addition, the anisotropic lattice relaxation occurred in the InGaN active layer. The elimination of the hexagonal phase inclusions plays an important role for the realization of high performance devices.

Original languageEnglish
Pages (from-to)241-246
Number of pages6
JournalPhysica Status Solidi (A) Applied Research
Volume180
Issue number1
DOIs
Publication statusPublished - 2000 Jul 1
Externally publishedYes
Event3rd International Symposium on Blue Laser and Light Emitting Diodes (ISBLLED 2000) - Zeuthen/Berlin, Ger
Duration: 2000 Mar 62000 Mar 10

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics

Fingerprint Dive into the research topics of 'Cubic InGaN/GaN double-heterostructure light emitting diodes grown on GaAs (001) substrates by MOVPE'. Together they form a unique fingerprint.

  • Cite this