Current-perpendicular-to-plane spin valves (SVs) with a new Heusler alloy of Co2 Mn (Ga0.5Sn0.5) (CMGS) as magnetic layers and an Ag spacer have been investigated. Magnetoresistance (MR) values of 8.8% and 17.2% and resistance change-area product (ΔRA) of 4.0 m μ m2 and 6.5 m μ m2 were measured at 300 K and 12 K, respectively. Transmission electron microscopy observations have revealed that the CMGS magnetic layer was ordered to the B2 structure for the SV annealed at 400 °C. Higher annealing temperature led to the degradation of the multilayer structure, resulting in lower MR and ΔRA values regardless of the L 21 structure of the CMGS layer. This suggests that MR properties may be enhanced further if the thermal stability of the multilayer structure is improved.