Development of a stimuli-responsive polymer nanocomposite toward biologically optimized, MEMS-based neural probes

A. E. Hess, J. R. Capadona, K. Shanmuganathan, L. Hsu, S. J. Rowan, C. Weder, D. J. Tyler, C. A. Zorman

Research output: Contribution to journalArticle

54 Citations (Scopus)

Abstract

This paper reports the development of micromachining processes and mechanical evaluation of a stimuli-responsive, mechanically dynamic polymer nanocomposite for biomedical microsystems. This nanocomposite consists of a cellulose nanofiber network encased in a polyvinyl acetate matrix. Micromachined tensile testing structures fabricated from the nanocomposite displayed a reversible and switchable stiffness comparable to bulk samples, with a Young's modulus of 3420 MPa when dry, reducing to ∼20 MPa when wet, and a stiff-to-flexible transition time of ∼300 s. This mechanically dynamic behavior is particularly attractive for the development of adaptive intracortical probes that are sufficiently stiff to insert into the brain without buckling, but become highly compliant upon insertion. Along these lines, a micromachined neural probe incorporating parylene insulating/moisture barrier layers and Ti/Au electrodes was fabricated from the nanocomposite using a fabrication process designed specifically for this chemical- and temperature-sensitive material. It was found that the parylene layers only slightly increased the stiffness of the probe in the wet state in spite of its much higher Young's modulus. Furthermore, the Ti/Au electrodes exhibited impedance comparable to Au electrodes on conventional substrates. Swelling of the nanocomposite was highly anisotropic favoring the thickness dimension by a factor of 8 to 12, leading to excellent adhesion between the nanocomposite and parylene layers and no discernable deformation of the probes when deployed in deionized water.

Original languageEnglish
Article number054009
JournalJournal of Micromechanics and Microengineering
Volume21
Issue number5
DOIs
Publication statusPublished - 2011 May
Externally publishedYes

Fingerprint

MEMS
Nanocomposites
Polymers
Electrodes
Elastic moduli
Stiffness
Polyvinyl acetates
Deionized water
Microsystems
Tensile testing
Micromachining
Nanofibers
Cellulose
Buckling
Swelling
Brain
Moisture
Adhesion
Fabrication
Substrates

ASJC Scopus subject areas

  • Mechanical Engineering
  • Electrical and Electronic Engineering
  • Mechanics of Materials
  • Electronic, Optical and Magnetic Materials

Cite this

Development of a stimuli-responsive polymer nanocomposite toward biologically optimized, MEMS-based neural probes. / Hess, A. E.; Capadona, J. R.; Shanmuganathan, K.; Hsu, L.; Rowan, S. J.; Weder, C.; Tyler, D. J.; Zorman, C. A.

In: Journal of Micromechanics and Microengineering, Vol. 21, No. 5, 054009, 05.2011.

Research output: Contribution to journalArticle

Hess, A. E. ; Capadona, J. R. ; Shanmuganathan, K. ; Hsu, L. ; Rowan, S. J. ; Weder, C. ; Tyler, D. J. ; Zorman, C. A. / Development of a stimuli-responsive polymer nanocomposite toward biologically optimized, MEMS-based neural probes. In: Journal of Micromechanics and Microengineering. 2011 ; Vol. 21, No. 5.
@article{ff9df0d415b94d4b91aa74e63881c953,
title = "Development of a stimuli-responsive polymer nanocomposite toward biologically optimized, MEMS-based neural probes",
abstract = "This paper reports the development of micromachining processes and mechanical evaluation of a stimuli-responsive, mechanically dynamic polymer nanocomposite for biomedical microsystems. This nanocomposite consists of a cellulose nanofiber network encased in a polyvinyl acetate matrix. Micromachined tensile testing structures fabricated from the nanocomposite displayed a reversible and switchable stiffness comparable to bulk samples, with a Young's modulus of 3420 MPa when dry, reducing to ∼20 MPa when wet, and a stiff-to-flexible transition time of ∼300 s. This mechanically dynamic behavior is particularly attractive for the development of adaptive intracortical probes that are sufficiently stiff to insert into the brain without buckling, but become highly compliant upon insertion. Along these lines, a micromachined neural probe incorporating parylene insulating/moisture barrier layers and Ti/Au electrodes was fabricated from the nanocomposite using a fabrication process designed specifically for this chemical- and temperature-sensitive material. It was found that the parylene layers only slightly increased the stiffness of the probe in the wet state in spite of its much higher Young's modulus. Furthermore, the Ti/Au electrodes exhibited impedance comparable to Au electrodes on conventional substrates. Swelling of the nanocomposite was highly anisotropic favoring the thickness dimension by a factor of 8 to 12, leading to excellent adhesion between the nanocomposite and parylene layers and no discernable deformation of the probes when deployed in deionized water.",
author = "Hess, {A. E.} and Capadona, {J. R.} and K. Shanmuganathan and L. Hsu and Rowan, {S. J.} and C. Weder and Tyler, {D. J.} and Zorman, {C. A.}",
year = "2011",
month = "5",
doi = "10.1088/0960-1317/21/5/054009",
language = "English",
volume = "21",
journal = "Journal of Micromechanics and Microengineering",
issn = "0960-1317",
publisher = "IOP Publishing Ltd.",
number = "5",

}

TY - JOUR

T1 - Development of a stimuli-responsive polymer nanocomposite toward biologically optimized, MEMS-based neural probes

AU - Hess, A. E.

AU - Capadona, J. R.

AU - Shanmuganathan, K.

AU - Hsu, L.

AU - Rowan, S. J.

AU - Weder, C.

AU - Tyler, D. J.

AU - Zorman, C. A.

PY - 2011/5

Y1 - 2011/5

N2 - This paper reports the development of micromachining processes and mechanical evaluation of a stimuli-responsive, mechanically dynamic polymer nanocomposite for biomedical microsystems. This nanocomposite consists of a cellulose nanofiber network encased in a polyvinyl acetate matrix. Micromachined tensile testing structures fabricated from the nanocomposite displayed a reversible and switchable stiffness comparable to bulk samples, with a Young's modulus of 3420 MPa when dry, reducing to ∼20 MPa when wet, and a stiff-to-flexible transition time of ∼300 s. This mechanically dynamic behavior is particularly attractive for the development of adaptive intracortical probes that are sufficiently stiff to insert into the brain without buckling, but become highly compliant upon insertion. Along these lines, a micromachined neural probe incorporating parylene insulating/moisture barrier layers and Ti/Au electrodes was fabricated from the nanocomposite using a fabrication process designed specifically for this chemical- and temperature-sensitive material. It was found that the parylene layers only slightly increased the stiffness of the probe in the wet state in spite of its much higher Young's modulus. Furthermore, the Ti/Au electrodes exhibited impedance comparable to Au electrodes on conventional substrates. Swelling of the nanocomposite was highly anisotropic favoring the thickness dimension by a factor of 8 to 12, leading to excellent adhesion between the nanocomposite and parylene layers and no discernable deformation of the probes when deployed in deionized water.

AB - This paper reports the development of micromachining processes and mechanical evaluation of a stimuli-responsive, mechanically dynamic polymer nanocomposite for biomedical microsystems. This nanocomposite consists of a cellulose nanofiber network encased in a polyvinyl acetate matrix. Micromachined tensile testing structures fabricated from the nanocomposite displayed a reversible and switchable stiffness comparable to bulk samples, with a Young's modulus of 3420 MPa when dry, reducing to ∼20 MPa when wet, and a stiff-to-flexible transition time of ∼300 s. This mechanically dynamic behavior is particularly attractive for the development of adaptive intracortical probes that are sufficiently stiff to insert into the brain without buckling, but become highly compliant upon insertion. Along these lines, a micromachined neural probe incorporating parylene insulating/moisture barrier layers and Ti/Au electrodes was fabricated from the nanocomposite using a fabrication process designed specifically for this chemical- and temperature-sensitive material. It was found that the parylene layers only slightly increased the stiffness of the probe in the wet state in spite of its much higher Young's modulus. Furthermore, the Ti/Au electrodes exhibited impedance comparable to Au electrodes on conventional substrates. Swelling of the nanocomposite was highly anisotropic favoring the thickness dimension by a factor of 8 to 12, leading to excellent adhesion between the nanocomposite and parylene layers and no discernable deformation of the probes when deployed in deionized water.

UR - http://www.scopus.com/inward/record.url?scp=79955811896&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=79955811896&partnerID=8YFLogxK

U2 - 10.1088/0960-1317/21/5/054009

DO - 10.1088/0960-1317/21/5/054009

M3 - Article

AN - SCOPUS:79955811896

VL - 21

JO - Journal of Micromechanics and Microengineering

JF - Journal of Micromechanics and Microengineering

SN - 0960-1317

IS - 5

M1 - 054009

ER -