Effect of lead and tin additives on surface morphology evolution of electrodeposited zinc

Tomohiro Otani, Yasuhiro Fukunaka, Takayuki Homma

    Research output: Contribution to journalArticle

    7 Citations (Scopus)

    Abstract

    Effects of Pb and Sn additives on electrodeposition of Zn were investigated for the applications in Zn secondary battery, focused on their roles on morphological evolution. Similarly to well-known effect of Pb addition to smoothly electrodeposit Zn film surface, Sn also exhibited to suppress the formation of mossy structures, which were highly filamentous Zn electrodeposits to cause frequently battery failure. Pb significantly shifted deposition potential of Zn to negative value at concentration less than 1.0 mmol dm−3, while Sn showed no substantial effect even at 50 mmol dm−3. The morphological evolution analysis demonstrated that the addition of 1.0 mmol dm−3 Pb significantly altered nucleation behavior of Zn at initial stages of deposition; stacking of layer-like structures (microsteps) were altered to discrete and uniform nuclei of Zn preferentially oriented to (002) direction. In contrast, with Sn additive, morphological features at the initial stage of deposition were similar to that without additive. However, microsteps evolution was gradually suppressed and relatively strong (002) texture of electrodeposited Zn was mitigated by Sn addition. These results suggested that the beneficial roles of Pb and Sn addition on Zn morphological evolution were ascribed to different reasons; Pb diminished the active growth sites of Zn surface by suppressing the deposition reaction of Zn, while Sn suppressed microsteps evolution by different texture evolution of Zn.

    Original languageEnglish
    Pages (from-to)364-372
    Number of pages9
    JournalElectrochimica Acta
    Volume242
    DOIs
    Publication statusPublished - 2017 Jul 10

    Fingerprint

    Tin
    Surface morphology
    Zinc
    Lead
    Textures
    Secondary batteries
    Electrodeposition
    Nucleation

    Keywords

    • Additive
    • Mossy structures
    • Zn batteries

    ASJC Scopus subject areas

    • Chemical Engineering(all)
    • Electrochemistry

    Cite this

    Effect of lead and tin additives on surface morphology evolution of electrodeposited zinc. / Otani, Tomohiro; Fukunaka, Yasuhiro; Homma, Takayuki.

    In: Electrochimica Acta, Vol. 242, 10.07.2017, p. 364-372.

    Research output: Contribution to journalArticle

    @article{d9aa0e332c094678a653db0e44b6a1e1,
    title = "Effect of lead and tin additives on surface morphology evolution of electrodeposited zinc",
    abstract = "Effects of Pb and Sn additives on electrodeposition of Zn were investigated for the applications in Zn secondary battery, focused on their roles on morphological evolution. Similarly to well-known effect of Pb addition to smoothly electrodeposit Zn film surface, Sn also exhibited to suppress the formation of mossy structures, which were highly filamentous Zn electrodeposits to cause frequently battery failure. Pb significantly shifted deposition potential of Zn to negative value at concentration less than 1.0 mmol dm−3, while Sn showed no substantial effect even at 50 mmol dm−3. The morphological evolution analysis demonstrated that the addition of 1.0 mmol dm−3 Pb significantly altered nucleation behavior of Zn at initial stages of deposition; stacking of layer-like structures (microsteps) were altered to discrete and uniform nuclei of Zn preferentially oriented to (002) direction. In contrast, with Sn additive, morphological features at the initial stage of deposition were similar to that without additive. However, microsteps evolution was gradually suppressed and relatively strong (002) texture of electrodeposited Zn was mitigated by Sn addition. These results suggested that the beneficial roles of Pb and Sn addition on Zn morphological evolution were ascribed to different reasons; Pb diminished the active growth sites of Zn surface by suppressing the deposition reaction of Zn, while Sn suppressed microsteps evolution by different texture evolution of Zn.",
    keywords = "Additive, Mossy structures, Zn batteries",
    author = "Tomohiro Otani and Yasuhiro Fukunaka and Takayuki Homma",
    year = "2017",
    month = "7",
    day = "10",
    doi = "10.1016/j.electacta.2017.04.130",
    language = "English",
    volume = "242",
    pages = "364--372",
    journal = "Electrochimica Acta",
    issn = "0013-4686",
    publisher = "Elsevier Limited",

    }

    TY - JOUR

    T1 - Effect of lead and tin additives on surface morphology evolution of electrodeposited zinc

    AU - Otani, Tomohiro

    AU - Fukunaka, Yasuhiro

    AU - Homma, Takayuki

    PY - 2017/7/10

    Y1 - 2017/7/10

    N2 - Effects of Pb and Sn additives on electrodeposition of Zn were investigated for the applications in Zn secondary battery, focused on their roles on morphological evolution. Similarly to well-known effect of Pb addition to smoothly electrodeposit Zn film surface, Sn also exhibited to suppress the formation of mossy structures, which were highly filamentous Zn electrodeposits to cause frequently battery failure. Pb significantly shifted deposition potential of Zn to negative value at concentration less than 1.0 mmol dm−3, while Sn showed no substantial effect even at 50 mmol dm−3. The morphological evolution analysis demonstrated that the addition of 1.0 mmol dm−3 Pb significantly altered nucleation behavior of Zn at initial stages of deposition; stacking of layer-like structures (microsteps) were altered to discrete and uniform nuclei of Zn preferentially oriented to (002) direction. In contrast, with Sn additive, morphological features at the initial stage of deposition were similar to that without additive. However, microsteps evolution was gradually suppressed and relatively strong (002) texture of electrodeposited Zn was mitigated by Sn addition. These results suggested that the beneficial roles of Pb and Sn addition on Zn morphological evolution were ascribed to different reasons; Pb diminished the active growth sites of Zn surface by suppressing the deposition reaction of Zn, while Sn suppressed microsteps evolution by different texture evolution of Zn.

    AB - Effects of Pb and Sn additives on electrodeposition of Zn were investigated for the applications in Zn secondary battery, focused on their roles on morphological evolution. Similarly to well-known effect of Pb addition to smoothly electrodeposit Zn film surface, Sn also exhibited to suppress the formation of mossy structures, which were highly filamentous Zn electrodeposits to cause frequently battery failure. Pb significantly shifted deposition potential of Zn to negative value at concentration less than 1.0 mmol dm−3, while Sn showed no substantial effect even at 50 mmol dm−3. The morphological evolution analysis demonstrated that the addition of 1.0 mmol dm−3 Pb significantly altered nucleation behavior of Zn at initial stages of deposition; stacking of layer-like structures (microsteps) were altered to discrete and uniform nuclei of Zn preferentially oriented to (002) direction. In contrast, with Sn additive, morphological features at the initial stage of deposition were similar to that without additive. However, microsteps evolution was gradually suppressed and relatively strong (002) texture of electrodeposited Zn was mitigated by Sn addition. These results suggested that the beneficial roles of Pb and Sn addition on Zn morphological evolution were ascribed to different reasons; Pb diminished the active growth sites of Zn surface by suppressing the deposition reaction of Zn, while Sn suppressed microsteps evolution by different texture evolution of Zn.

    KW - Additive

    KW - Mossy structures

    KW - Zn batteries

    UR - http://www.scopus.com/inward/record.url?scp=85019262143&partnerID=8YFLogxK

    UR - http://www.scopus.com/inward/citedby.url?scp=85019262143&partnerID=8YFLogxK

    U2 - 10.1016/j.electacta.2017.04.130

    DO - 10.1016/j.electacta.2017.04.130

    M3 - Article

    VL - 242

    SP - 364

    EP - 372

    JO - Electrochimica Acta

    JF - Electrochimica Acta

    SN - 0013-4686

    ER -