Effect of temperature and time of wetness on corrosion of carbon steel under insulation

Yukinori Yanase, Yuichi Ishikawa, Jun'ichi Sakai

    Research output: Contribution to journalArticle

    1 Citation (Scopus)

    Abstract

    This study was carried out to clarify the effect of temperature and time of wetness on corrosion of carbon steel under insulation. The specimen used was carbon steel SS400. In this test, the specimen was covered with calcium silicate insulation and heated in a temperature range from 40 to 200°C by an electric heater. Corrosion test was conducted by pouring deionized water of 25 to 50 ml into the insulation. The time of wetness on the steel surface under the insulation was evaluated using the ACM sensor. The results of the corrosion test showed that corrosion was not found at temperatures above 100°C. On the other hand, corrosion occurred locally at temperatures between 40 ∼ 90°C and the corrosion depth became deeper with decreasing steel surface temperature. The time of wetness of the steel surface measured with the ACM sensor increased with decreasing steel surface temperature. This indicates that the increase in time of wetness on the steel surface has more significant effect on corrosion of the steel under insulation than the increase in the corrosion reactivity with increasing temperature.

    Original languageEnglish
    Pages (from-to)329-332
    Number of pages4
    JournalZairyo to Kankyo/ Corrosion Engineering
    Volume63
    Issue number5
    Publication statusPublished - 2014

    Fingerprint

    Carbon steel
    Insulation
    Steel
    Corrosion
    Temperature
    Calcium silicate
    Deionized water
    Sensors

    Keywords

    • ACM sensor
    • Carbon steel
    • Corrosion under insulation
    • Temperature
    • Time of wetness

    ASJC Scopus subject areas

    • Electrochemistry
    • Materials Chemistry
    • Metals and Alloys
    • Surfaces, Coatings and Films

    Cite this

    Effect of temperature and time of wetness on corrosion of carbon steel under insulation. / Yanase, Yukinori; Ishikawa, Yuichi; Sakai, Jun'ichi.

    In: Zairyo to Kankyo/ Corrosion Engineering, Vol. 63, No. 5, 2014, p. 329-332.

    Research output: Contribution to journalArticle

    Yanase, Yukinori ; Ishikawa, Yuichi ; Sakai, Jun'ichi. / Effect of temperature and time of wetness on corrosion of carbon steel under insulation. In: Zairyo to Kankyo/ Corrosion Engineering. 2014 ; Vol. 63, No. 5. pp. 329-332.
    @article{14a446258fcc408dbf48913869488c0d,
    title = "Effect of temperature and time of wetness on corrosion of carbon steel under insulation",
    abstract = "This study was carried out to clarify the effect of temperature and time of wetness on corrosion of carbon steel under insulation. The specimen used was carbon steel SS400. In this test, the specimen was covered with calcium silicate insulation and heated in a temperature range from 40 to 200°C by an electric heater. Corrosion test was conducted by pouring deionized water of 25 to 50 ml into the insulation. The time of wetness on the steel surface under the insulation was evaluated using the ACM sensor. The results of the corrosion test showed that corrosion was not found at temperatures above 100°C. On the other hand, corrosion occurred locally at temperatures between 40 ∼ 90°C and the corrosion depth became deeper with decreasing steel surface temperature. The time of wetness of the steel surface measured with the ACM sensor increased with decreasing steel surface temperature. This indicates that the increase in time of wetness on the steel surface has more significant effect on corrosion of the steel under insulation than the increase in the corrosion reactivity with increasing temperature.",
    keywords = "ACM sensor, Carbon steel, Corrosion under insulation, Temperature, Time of wetness",
    author = "Yukinori Yanase and Yuichi Ishikawa and Jun'ichi Sakai",
    year = "2014",
    language = "English",
    volume = "63",
    pages = "329--332",
    journal = "Corrosion Engineering",
    issn = "0917-0480",
    publisher = "Japan Society of Corrosion Engineering",
    number = "5",

    }

    TY - JOUR

    T1 - Effect of temperature and time of wetness on corrosion of carbon steel under insulation

    AU - Yanase, Yukinori

    AU - Ishikawa, Yuichi

    AU - Sakai, Jun'ichi

    PY - 2014

    Y1 - 2014

    N2 - This study was carried out to clarify the effect of temperature and time of wetness on corrosion of carbon steel under insulation. The specimen used was carbon steel SS400. In this test, the specimen was covered with calcium silicate insulation and heated in a temperature range from 40 to 200°C by an electric heater. Corrosion test was conducted by pouring deionized water of 25 to 50 ml into the insulation. The time of wetness on the steel surface under the insulation was evaluated using the ACM sensor. The results of the corrosion test showed that corrosion was not found at temperatures above 100°C. On the other hand, corrosion occurred locally at temperatures between 40 ∼ 90°C and the corrosion depth became deeper with decreasing steel surface temperature. The time of wetness of the steel surface measured with the ACM sensor increased with decreasing steel surface temperature. This indicates that the increase in time of wetness on the steel surface has more significant effect on corrosion of the steel under insulation than the increase in the corrosion reactivity with increasing temperature.

    AB - This study was carried out to clarify the effect of temperature and time of wetness on corrosion of carbon steel under insulation. The specimen used was carbon steel SS400. In this test, the specimen was covered with calcium silicate insulation and heated in a temperature range from 40 to 200°C by an electric heater. Corrosion test was conducted by pouring deionized water of 25 to 50 ml into the insulation. The time of wetness on the steel surface under the insulation was evaluated using the ACM sensor. The results of the corrosion test showed that corrosion was not found at temperatures above 100°C. On the other hand, corrosion occurred locally at temperatures between 40 ∼ 90°C and the corrosion depth became deeper with decreasing steel surface temperature. The time of wetness of the steel surface measured with the ACM sensor increased with decreasing steel surface temperature. This indicates that the increase in time of wetness on the steel surface has more significant effect on corrosion of the steel under insulation than the increase in the corrosion reactivity with increasing temperature.

    KW - ACM sensor

    KW - Carbon steel

    KW - Corrosion under insulation

    KW - Temperature

    KW - Time of wetness

    UR - http://www.scopus.com/inward/record.url?scp=84918548289&partnerID=8YFLogxK

    UR - http://www.scopus.com/inward/citedby.url?scp=84918548289&partnerID=8YFLogxK

    M3 - Article

    VL - 63

    SP - 329

    EP - 332

    JO - Corrosion Engineering

    JF - Corrosion Engineering

    SN - 0917-0480

    IS - 5

    ER -