Electrochemical preparation of soft magnetic CoNiFeS film with high saturation magnetic flux density and high resistivity

M. Takai, K. Hayashi, M. Aoyagi, T. Osaka

Research output: Contribution to journalArticle

62 Citations (Scopus)

Abstract

A soft magnetic CoNiFeS film as a write head core material for the next generation was prepared by electrodeposition. In this system, thiourea was used as an additive in the CoNiFe ternary alloy plating bath. The most suitable magnetic properties were obtained at the film composition of (Co73Ni12Fe15)99.1S0.9 [atomic percent (a/o)] with a high saturation magnetic flux density (Bs) of 1.7 T, a high resistivity (ρ) of 51 μΩ cm, and a low saturation magnetostriction (λs) of 4.4 × 10-6. The film consisted of fine minute crystal grains 5 to 10 nm in diameter. The S content of ca. 0.9 a/o is believed to be responsible for the formation of small crystal grains with low coercivity and high resistivity.

Original languageEnglish
Pages (from-to)L203-L204
JournalJournal of the Electrochemical Society
Volume144
Issue number7
DOIs
Publication statusPublished - 1997 Jul

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Renewable Energy, Sustainability and the Environment
  • Surfaces, Coatings and Films
  • Electrochemistry
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Electrochemical preparation of soft magnetic CoNiFeS film with high saturation magnetic flux density and high resistivity'. Together they form a unique fingerprint.

  • Cite this