Evaluation of transverse crack initiation in cross-ply CFRP laminates under fatigue loading

Keigo Takamura, Atsushi Hosoi, Narumichi Sato, Hiroyuki Kawada

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

In this study, transverse crack initiation in cross-ply CFRP laminates under fatigue loading was evaluated focusing on the transverse crack growth and saturation. The number of cycles that a transverse crack initiates was predicted by the analytical model on the basis of the modified Paris law. In addition, the lower threshold of the transverse crack formation was researched by a modified Paris-law, and the fatigue limit of the transverse crack initiation was evaluated by calculating the stress applied in 90° layer where the increase of the transverse cracks was saturated. Moreover, transverse crack was observed by using scanning electron microscope (SEM) in order to investigate the mechanism of transverse crack initiation. As the results, the analytical results for predicting the transverse crack initiation showed good agreement with the experimental results. Moreover, it was shown that the lower threshold of the transverse crack formation existed, and that the stress applied in 90° layer at saturation state was almost equivalent to the fatigue limit of the transverse crack initiation from the experimental results. From the observation with SEM, it was found that the initiation of the transverse crack under fatigue loading depended on the interface property between fiber and matrix.

Original languageEnglish
Pages (from-to)1123-1134
Number of pages12
JournalNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
Volume77
Issue number779
DOIs
Publication statusPublished - 2011
Externally publishedYes

Fingerprint

Carbon fiber reinforced plastics
Crack initiation
Laminates
Fatigue of materials
Cracks
Electron microscopes
Scanning
carbon fiber reinforced plastic
Analytical models
Crack propagation
Fibers

Keywords

  • CFRP
  • Fatigue
  • Initiation
  • Prediction
  • Transverse crack

ASJC Scopus subject areas

  • Mechanical Engineering
  • Mechanics of Materials
  • Materials Science(all)

Cite this

@article{01ae0a40067c494bb38c8f0ed83574a7,
title = "Evaluation of transverse crack initiation in cross-ply CFRP laminates under fatigue loading",
abstract = "In this study, transverse crack initiation in cross-ply CFRP laminates under fatigue loading was evaluated focusing on the transverse crack growth and saturation. The number of cycles that a transverse crack initiates was predicted by the analytical model on the basis of the modified Paris law. In addition, the lower threshold of the transverse crack formation was researched by a modified Paris-law, and the fatigue limit of the transverse crack initiation was evaluated by calculating the stress applied in 90° layer where the increase of the transverse cracks was saturated. Moreover, transverse crack was observed by using scanning electron microscope (SEM) in order to investigate the mechanism of transverse crack initiation. As the results, the analytical results for predicting the transverse crack initiation showed good agreement with the experimental results. Moreover, it was shown that the lower threshold of the transverse crack formation existed, and that the stress applied in 90° layer at saturation state was almost equivalent to the fatigue limit of the transverse crack initiation from the experimental results. From the observation with SEM, it was found that the initiation of the transverse crack under fatigue loading depended on the interface property between fiber and matrix.",
keywords = "CFRP, Fatigue, Initiation, Prediction, Transverse crack",
author = "Keigo Takamura and Atsushi Hosoi and Narumichi Sato and Hiroyuki Kawada",
year = "2011",
doi = "10.1299/kikaia.77.1123",
language = "English",
volume = "77",
pages = "1123--1134",
journal = "Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A",
issn = "0387-5008",
publisher = "Japan Society of Mechanical Engineers",
number = "779",

}

TY - JOUR

T1 - Evaluation of transverse crack initiation in cross-ply CFRP laminates under fatigue loading

AU - Takamura, Keigo

AU - Hosoi, Atsushi

AU - Sato, Narumichi

AU - Kawada, Hiroyuki

PY - 2011

Y1 - 2011

N2 - In this study, transverse crack initiation in cross-ply CFRP laminates under fatigue loading was evaluated focusing on the transverse crack growth and saturation. The number of cycles that a transverse crack initiates was predicted by the analytical model on the basis of the modified Paris law. In addition, the lower threshold of the transverse crack formation was researched by a modified Paris-law, and the fatigue limit of the transverse crack initiation was evaluated by calculating the stress applied in 90° layer where the increase of the transverse cracks was saturated. Moreover, transverse crack was observed by using scanning electron microscope (SEM) in order to investigate the mechanism of transverse crack initiation. As the results, the analytical results for predicting the transverse crack initiation showed good agreement with the experimental results. Moreover, it was shown that the lower threshold of the transverse crack formation existed, and that the stress applied in 90° layer at saturation state was almost equivalent to the fatigue limit of the transverse crack initiation from the experimental results. From the observation with SEM, it was found that the initiation of the transverse crack under fatigue loading depended on the interface property between fiber and matrix.

AB - In this study, transverse crack initiation in cross-ply CFRP laminates under fatigue loading was evaluated focusing on the transverse crack growth and saturation. The number of cycles that a transverse crack initiates was predicted by the analytical model on the basis of the modified Paris law. In addition, the lower threshold of the transverse crack formation was researched by a modified Paris-law, and the fatigue limit of the transverse crack initiation was evaluated by calculating the stress applied in 90° layer where the increase of the transverse cracks was saturated. Moreover, transverse crack was observed by using scanning electron microscope (SEM) in order to investigate the mechanism of transverse crack initiation. As the results, the analytical results for predicting the transverse crack initiation showed good agreement with the experimental results. Moreover, it was shown that the lower threshold of the transverse crack formation existed, and that the stress applied in 90° layer at saturation state was almost equivalent to the fatigue limit of the transverse crack initiation from the experimental results. From the observation with SEM, it was found that the initiation of the transverse crack under fatigue loading depended on the interface property between fiber and matrix.

KW - CFRP

KW - Fatigue

KW - Initiation

KW - Prediction

KW - Transverse crack

UR - http://www.scopus.com/inward/record.url?scp=84856497005&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84856497005&partnerID=8YFLogxK

U2 - 10.1299/kikaia.77.1123

DO - 10.1299/kikaia.77.1123

M3 - Article

AN - SCOPUS:84856497005

VL - 77

SP - 1123

EP - 1134

JO - Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A

JF - Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A

SN - 0387-5008

IS - 779

ER -