Heterogeneous catalytic activity of NiO-silica composites designated with cubic Pm3n cage nanostructures

Sherif A. El-Safty, Yoshimichi Kiyozumi, Takaaki Hanaoka, Fujio Mizukami

Research output: Contribution to journalArticle

23 Citations (Scopus)

Abstract

The fabrication of nanomaterials with the active network sites has led to efficient transport and easier diffusion of guest species in the catalytic application. In this regard, the NiO-supported cage monoliths show evidence to act as effective catalysts toward the oxidation of organic pollutants. Here, the cage-like NiO-silica catalyst with large particle size, cage-like pores, and ordered cubic Pm3n (HOM-9) structures could be fabricated by a simple, in short period (∼5 min), and direct strategy in which microemulsion liquid crystalline phase of Brij 56 (C16EO10) surfactant was used as a template. Our synthetic strategy revealed that the nickel oxide nanoparticles were wrapped onto the pore surface matrices of the cubic Pm3n monoliths, indicating the simplicity and flexibility to control the geometry, morphology and dispersion of particles. No significant change in the cubic Pm3n (NiO/HOM-9) phase structures was evident by using this synthetic manipulation; however, high nickel contents up to Si/Ni ratios ∼1 were added to the phase composition domains. Results from the analysis techniques including XRD, N2 isotherms, TEM, XPS, and EDX revealed that the NiO nanoparticles with irregular sizes might be embedded, to some extent, into the pore cavity, particularly with low content of NiO. In turn, with low Si/Ni ratios, The NiO crystallite particles underwent the anisotropic growth to larger sizes (∼15 nm) resulted from the aggregation effect, leading to the difficulty to be wrapped into the pore cavity. Practically important results were that the NiO-supported cage monoliths were used as effective catalysts for the oxidation of aminophenols in aqueous solution. However, among all NiO-supported amorphous and ordered silica materials, the NiO/HOM-9 catalyst with open, uniform pore-cage architectures, high surface area and large pore volumes allowed efficient adsorption and diffusion of aminophenols to the active site of NiO clusters, leading to high degree of conversion and reaction rate. On such heterogeneous catalytic systems, the reaction affinity of aminophenols was substantially affected by the structural feature of the catalysts, amount and degree of dispersion NiO particles onto the cubic cage pore surfaces, and the controlled temperature conditions.

Original languageEnglish
Pages (from-to)169-179
Number of pages11
JournalApplied Catalysis B: Environmental
Volume82
Issue number3-4
DOIs
Publication statusPublished - 2008 Aug 8
Externally publishedYes

Fingerprint

Silicon Dioxide
Nanostructures
Catalyst activity
Aminophenols
silica
catalyst
Silica
Catalysts
Composite materials
nickel
Cetomacrogol
cavity
Nanoparticles
Active networks
oxidation
Oxidation
Nickel oxide
Organic pollutants
Microemulsions
Phase structure

Keywords

  • Cage pores
  • Monoliths
  • NiO-supported catalysts
  • Organic pollutant
  • Oxidation reaction

ASJC Scopus subject areas

  • Catalysis
  • Process Chemistry and Technology
  • Environmental Chemistry

Cite this

Heterogeneous catalytic activity of NiO-silica composites designated with cubic Pm3n cage nanostructures. / El-Safty, Sherif A.; Kiyozumi, Yoshimichi; Hanaoka, Takaaki; Mizukami, Fujio.

In: Applied Catalysis B: Environmental, Vol. 82, No. 3-4, 08.08.2008, p. 169-179.

Research output: Contribution to journalArticle

El-Safty, Sherif A. ; Kiyozumi, Yoshimichi ; Hanaoka, Takaaki ; Mizukami, Fujio. / Heterogeneous catalytic activity of NiO-silica composites designated with cubic Pm3n cage nanostructures. In: Applied Catalysis B: Environmental. 2008 ; Vol. 82, No. 3-4. pp. 169-179.
@article{a1c6f15c56c3468f9e0f269f4f0eef1a,
title = "Heterogeneous catalytic activity of NiO-silica composites designated with cubic Pm3n cage nanostructures",
abstract = "The fabrication of nanomaterials with the active network sites has led to efficient transport and easier diffusion of guest species in the catalytic application. In this regard, the NiO-supported cage monoliths show evidence to act as effective catalysts toward the oxidation of organic pollutants. Here, the cage-like NiO-silica catalyst with large particle size, cage-like pores, and ordered cubic Pm3n (HOM-9) structures could be fabricated by a simple, in short period (∼5 min), and direct strategy in which microemulsion liquid crystalline phase of Brij 56 (C16EO10) surfactant was used as a template. Our synthetic strategy revealed that the nickel oxide nanoparticles were wrapped onto the pore surface matrices of the cubic Pm3n monoliths, indicating the simplicity and flexibility to control the geometry, morphology and dispersion of particles. No significant change in the cubic Pm3n (NiO/HOM-9) phase structures was evident by using this synthetic manipulation; however, high nickel contents up to Si/Ni ratios ∼1 were added to the phase composition domains. Results from the analysis techniques including XRD, N2 isotherms, TEM, XPS, and EDX revealed that the NiO nanoparticles with irregular sizes might be embedded, to some extent, into the pore cavity, particularly with low content of NiO. In turn, with low Si/Ni ratios, The NiO crystallite particles underwent the anisotropic growth to larger sizes (∼15 nm) resulted from the aggregation effect, leading to the difficulty to be wrapped into the pore cavity. Practically important results were that the NiO-supported cage monoliths were used as effective catalysts for the oxidation of aminophenols in aqueous solution. However, among all NiO-supported amorphous and ordered silica materials, the NiO/HOM-9 catalyst with open, uniform pore-cage architectures, high surface area and large pore volumes allowed efficient adsorption and diffusion of aminophenols to the active site of NiO clusters, leading to high degree of conversion and reaction rate. On such heterogeneous catalytic systems, the reaction affinity of aminophenols was substantially affected by the structural feature of the catalysts, amount and degree of dispersion NiO particles onto the cubic cage pore surfaces, and the controlled temperature conditions.",
keywords = "Cage pores, Monoliths, NiO-supported catalysts, Organic pollutant, Oxidation reaction",
author = "El-Safty, {Sherif A.} and Yoshimichi Kiyozumi and Takaaki Hanaoka and Fujio Mizukami",
year = "2008",
month = "8",
day = "8",
doi = "10.1016/j.apcatb.2008.01.027",
language = "English",
volume = "82",
pages = "169--179",
journal = "Applied Catalysis B: Environmental",
issn = "0926-3373",
publisher = "Elsevier",
number = "3-4",

}

TY - JOUR

T1 - Heterogeneous catalytic activity of NiO-silica composites designated with cubic Pm3n cage nanostructures

AU - El-Safty, Sherif A.

AU - Kiyozumi, Yoshimichi

AU - Hanaoka, Takaaki

AU - Mizukami, Fujio

PY - 2008/8/8

Y1 - 2008/8/8

N2 - The fabrication of nanomaterials with the active network sites has led to efficient transport and easier diffusion of guest species in the catalytic application. In this regard, the NiO-supported cage monoliths show evidence to act as effective catalysts toward the oxidation of organic pollutants. Here, the cage-like NiO-silica catalyst with large particle size, cage-like pores, and ordered cubic Pm3n (HOM-9) structures could be fabricated by a simple, in short period (∼5 min), and direct strategy in which microemulsion liquid crystalline phase of Brij 56 (C16EO10) surfactant was used as a template. Our synthetic strategy revealed that the nickel oxide nanoparticles were wrapped onto the pore surface matrices of the cubic Pm3n monoliths, indicating the simplicity and flexibility to control the geometry, morphology and dispersion of particles. No significant change in the cubic Pm3n (NiO/HOM-9) phase structures was evident by using this synthetic manipulation; however, high nickel contents up to Si/Ni ratios ∼1 were added to the phase composition domains. Results from the analysis techniques including XRD, N2 isotherms, TEM, XPS, and EDX revealed that the NiO nanoparticles with irregular sizes might be embedded, to some extent, into the pore cavity, particularly with low content of NiO. In turn, with low Si/Ni ratios, The NiO crystallite particles underwent the anisotropic growth to larger sizes (∼15 nm) resulted from the aggregation effect, leading to the difficulty to be wrapped into the pore cavity. Practically important results were that the NiO-supported cage monoliths were used as effective catalysts for the oxidation of aminophenols in aqueous solution. However, among all NiO-supported amorphous and ordered silica materials, the NiO/HOM-9 catalyst with open, uniform pore-cage architectures, high surface area and large pore volumes allowed efficient adsorption and diffusion of aminophenols to the active site of NiO clusters, leading to high degree of conversion and reaction rate. On such heterogeneous catalytic systems, the reaction affinity of aminophenols was substantially affected by the structural feature of the catalysts, amount and degree of dispersion NiO particles onto the cubic cage pore surfaces, and the controlled temperature conditions.

AB - The fabrication of nanomaterials with the active network sites has led to efficient transport and easier diffusion of guest species in the catalytic application. In this regard, the NiO-supported cage monoliths show evidence to act as effective catalysts toward the oxidation of organic pollutants. Here, the cage-like NiO-silica catalyst with large particle size, cage-like pores, and ordered cubic Pm3n (HOM-9) structures could be fabricated by a simple, in short period (∼5 min), and direct strategy in which microemulsion liquid crystalline phase of Brij 56 (C16EO10) surfactant was used as a template. Our synthetic strategy revealed that the nickel oxide nanoparticles were wrapped onto the pore surface matrices of the cubic Pm3n monoliths, indicating the simplicity and flexibility to control the geometry, morphology and dispersion of particles. No significant change in the cubic Pm3n (NiO/HOM-9) phase structures was evident by using this synthetic manipulation; however, high nickel contents up to Si/Ni ratios ∼1 were added to the phase composition domains. Results from the analysis techniques including XRD, N2 isotherms, TEM, XPS, and EDX revealed that the NiO nanoparticles with irregular sizes might be embedded, to some extent, into the pore cavity, particularly with low content of NiO. In turn, with low Si/Ni ratios, The NiO crystallite particles underwent the anisotropic growth to larger sizes (∼15 nm) resulted from the aggregation effect, leading to the difficulty to be wrapped into the pore cavity. Practically important results were that the NiO-supported cage monoliths were used as effective catalysts for the oxidation of aminophenols in aqueous solution. However, among all NiO-supported amorphous and ordered silica materials, the NiO/HOM-9 catalyst with open, uniform pore-cage architectures, high surface area and large pore volumes allowed efficient adsorption and diffusion of aminophenols to the active site of NiO clusters, leading to high degree of conversion and reaction rate. On such heterogeneous catalytic systems, the reaction affinity of aminophenols was substantially affected by the structural feature of the catalysts, amount and degree of dispersion NiO particles onto the cubic cage pore surfaces, and the controlled temperature conditions.

KW - Cage pores

KW - Monoliths

KW - NiO-supported catalysts

KW - Organic pollutant

KW - Oxidation reaction

UR - http://www.scopus.com/inward/record.url?scp=47249146920&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=47249146920&partnerID=8YFLogxK

U2 - 10.1016/j.apcatb.2008.01.027

DO - 10.1016/j.apcatb.2008.01.027

M3 - Article

VL - 82

SP - 169

EP - 179

JO - Applied Catalysis B: Environmental

JF - Applied Catalysis B: Environmental

SN - 0926-3373

IS - 3-4

ER -