Important factors for effective use of carbon nanotube matrices in electrochemical capacitor hybrid electrodes without binding additives

Ricardo Quintero, Dong Young Kim, Kei Hasegawa, Yuki Yamada, Atsuo Yamada, Suguru Noda

    Research output: Contribution to journalArticle

    10 Citations (Scopus)


    Various capacitive particles are currently available for use in electrochemical capacitors, but their electrical conductivities are typically low and require enhancement. Carbon nanotube (CNT) matrices can be used to fabricate self-supporting electrodes without binding or conducting additives. Herein, liquid dispersion and subsequent vacuum filtration were used to prepare thick (∼100 μm) hybrid electrodes of activated carbon (AC) and CNTs. Factors including CNT type, AC particle size, solvent, and surfactant strongly affected the capacitance and rate performance of the hybrid electrodes. Different solvents and types of CNTs were best suited for pure CNT electrodes and AC-CNT hybrid electrodes; single-wall CNTs (SWCNTs) with a strong dispersant produced CNT electrodes with the best performance among pure CNT electrodes. Meanwhile, few-wall CNTs (FWCNTs) with a weak dispersant produced AC-CNT hybrid electrodes with the best performance among hybrid electrodes. Addition of 10 wt% FWCNTs to AC yielded a self-supporting hybrid electrode with improved performance (132 F g-1, 58 F cm-3, 0.70 F cm-2 at 100 mV s-1) compared with that of a conventional AC electrode with conducting and binding additives (74 F g-1, 26 F cm-3, 0.60 F cm-2 at 100 mV s-1), and a pure electrode of expensive SWCNTs (52 F g-1, 26 F cm-3, 0.26 F cm-2 at 100 mV s-1). This journal is

    Original languageEnglish
    Pages (from-to)16101-16111
    Number of pages11
    JournalRSC Advances
    Issue number21
    Publication statusPublished - 2015


    ASJC Scopus subject areas

    • Chemical Engineering(all)
    • Chemistry(all)

    Cite this