Microstructual characterization of sputtered Pt-Ir coatings on Ni-base single crystal superalloy

Aya Suzuki, Masanori Harada, Yingna Wu, Hideyuki Murakami

Research output: Contribution to journalArticle

11 Citations (Scopus)

Abstract

Characterization of Pt-Ir alloy coatings on a Ni-base single crystal superalloy was carried out. Pt-Ir alloys with varied composition were sputter-deposited on TMS-82+, which were then subjected to annealing and Al-pack cementation treatments. It was found that all the as-deposited films consisted of Pt-Ir solid solutioned fee single phase, while the annealing treatment at 1423 K for 1 h drastically changed the microstructure, depending on the composition of coated layers. On the other hand, concentration profiles of alloying elements were not drastically changed by the Al-pack cementation process. It was also revealed that Ir addition increases the surface hardness of all the as-deposited, annealed, and aluminized specimens.

Original languageEnglish
Pages (from-to)1760-1763
Number of pages4
JournalMaterials Transactions
Volume46
Issue number8
DOIs
Publication statusPublished - 2005 Aug 1
Externally publishedYes

Fingerprint

cementation
heat resistant alloys
Superalloys
Single crystals
Annealing
coatings
Coatings
annealing
single crystals
Alloying elements
Chemical analysis
alloying
hardness
Hardness
microstructure
Microstructure
profiles
platinum-iridium alloy

Keywords

  • Aluminizing
  • Bond coat
  • Ni-base superalloy
  • Platinum-iridium

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Microstructual characterization of sputtered Pt-Ir coatings on Ni-base single crystal superalloy. / Suzuki, Aya; Harada, Masanori; Wu, Yingna; Murakami, Hideyuki.

In: Materials Transactions, Vol. 46, No. 8, 01.08.2005, p. 1760-1763.

Research output: Contribution to journalArticle

@article{6b2da73c84674ef9a25504bc02051e86,
title = "Microstructual characterization of sputtered Pt-Ir coatings on Ni-base single crystal superalloy",
abstract = "Characterization of Pt-Ir alloy coatings on a Ni-base single crystal superalloy was carried out. Pt-Ir alloys with varied composition were sputter-deposited on TMS-82+, which were then subjected to annealing and Al-pack cementation treatments. It was found that all the as-deposited films consisted of Pt-Ir solid solutioned fee single phase, while the annealing treatment at 1423 K for 1 h drastically changed the microstructure, depending on the composition of coated layers. On the other hand, concentration profiles of alloying elements were not drastically changed by the Al-pack cementation process. It was also revealed that Ir addition increases the surface hardness of all the as-deposited, annealed, and aluminized specimens.",
keywords = "Aluminizing, Bond coat, Ni-base superalloy, Platinum-iridium",
author = "Aya Suzuki and Masanori Harada and Yingna Wu and Hideyuki Murakami",
year = "2005",
month = "8",
day = "1",
doi = "10.2320/matertrans.46.1760",
language = "English",
volume = "46",
pages = "1760--1763",
journal = "Materials Transactions",
issn = "1345-9678",
publisher = "Japan Institute of Metals (JIM)",
number = "8",

}

TY - JOUR

T1 - Microstructual characterization of sputtered Pt-Ir coatings on Ni-base single crystal superalloy

AU - Suzuki, Aya

AU - Harada, Masanori

AU - Wu, Yingna

AU - Murakami, Hideyuki

PY - 2005/8/1

Y1 - 2005/8/1

N2 - Characterization of Pt-Ir alloy coatings on a Ni-base single crystal superalloy was carried out. Pt-Ir alloys with varied composition were sputter-deposited on TMS-82+, which were then subjected to annealing and Al-pack cementation treatments. It was found that all the as-deposited films consisted of Pt-Ir solid solutioned fee single phase, while the annealing treatment at 1423 K for 1 h drastically changed the microstructure, depending on the composition of coated layers. On the other hand, concentration profiles of alloying elements were not drastically changed by the Al-pack cementation process. It was also revealed that Ir addition increases the surface hardness of all the as-deposited, annealed, and aluminized specimens.

AB - Characterization of Pt-Ir alloy coatings on a Ni-base single crystal superalloy was carried out. Pt-Ir alloys with varied composition were sputter-deposited on TMS-82+, which were then subjected to annealing and Al-pack cementation treatments. It was found that all the as-deposited films consisted of Pt-Ir solid solutioned fee single phase, while the annealing treatment at 1423 K for 1 h drastically changed the microstructure, depending on the composition of coated layers. On the other hand, concentration profiles of alloying elements were not drastically changed by the Al-pack cementation process. It was also revealed that Ir addition increases the surface hardness of all the as-deposited, annealed, and aluminized specimens.

KW - Aluminizing

KW - Bond coat

KW - Ni-base superalloy

KW - Platinum-iridium

UR - http://www.scopus.com/inward/record.url?scp=26944465754&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=26944465754&partnerID=8YFLogxK

U2 - 10.2320/matertrans.46.1760

DO - 10.2320/matertrans.46.1760

M3 - Article

AN - SCOPUS:26944465754

VL - 46

SP - 1760

EP - 1763

JO - Materials Transactions

JF - Materials Transactions

SN - 1345-9678

IS - 8

ER -