Nanocrystallization of complex Fe23B6-type structure in glassy Fe-Co-B-Si-Nb alloy

Akihiko Hirata, Yoshihiko Hirotsu, Kenji Amiya, Nobuyuki Nishiyama, Akihisa Inoue

Research output: Contribution to journalArticle

47 Citations (Scopus)

Abstract

Local structural development in the bulk metallic glass (Fe0.5Co0.5)72B20Si4Nb4 on annealing has been investigated using transmission electron microscopy. Nanoscale crystalline grains with the Fe23B6-type structure were densely formed during annealing around the first crystallization temperature. In the state prior to the crystallization (below Tg), we found extended medium range ordered (MRO) regions as small as 2 nm with an extremely high density in the glass matrix. The nanocrystallized microstructure is presumably ascribed to the presence of the dense MRO regions. On the basis of nanobeam diffraction analysis, however, it was found that most of the MRO regions have no clear order of the Fe23B6-type structure. The clear Fe23B6 order was found in regions extending as large as 5 nm at a higher temperature (around Tg). A relationship between the structural change and the glass stability is discussed.

Original languageEnglish
Pages (from-to)491-497
Number of pages7
JournalIntermetallics
Volume16
Issue number4
DOIs
Publication statusPublished - 2008 Apr 1

Keywords

  • B. Glasses, metallic
  • F. Diffraction
  • F. Electron microscopy, transmission

ASJC Scopus subject areas

  • Chemistry(all)
  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Nanocrystallization of complex Fe<sub>23</sub>B<sub>6</sub>-type structure in glassy Fe-Co-B-Si-Nb alloy'. Together they form a unique fingerprint.

  • Cite this