Abstract
In the previous paper the transformation temperature of pure iron by super-rapid heating was reported. In the present study the ( alpha plus Fe//3C yields gamma ) A//c//1 transformation behavior in eutectoid steel by super-rapid heating at 0 similar 10**7 degree C/sec was investigated using the same method as used for pure iron. The main results obtained are as follows: (1) The heating cycles up to the heating rate of 10**7 degree C/sec were recorded by the PbS cell heat-radiater and the dilatometer, from which the ( alpha plus Fe//3C yields gamma ) transformation temperature was determined. (2) The increment of the transformation point from the equilibrium point (A//c//1) in the eutectoid steel with heating rate (0 similar 10**7 degree C/sec) was determined. The A(clf) transformation curve is split up into two steps and in the lamellar pearlite specimen A(clf) was detected around 1100 degree C at the heating rate of 10**7 degree C/sec.
| Original language | English |
|---|---|
| Pages (from-to) | 24-28 |
| Number of pages | 5 |
| Journal | Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals |
| Volume | 39 |
| Issue number | 1 |
| Publication status | Published - 1975 Jan |
| Externally published | Yes |
Fingerprint
ASJC Scopus subject areas
- Metals and Alloys
Cite this
ON THE TRANSFORMATION IN EUTECTOID STEEL BY SUPER-RAPID HEATING. / Miwa, Yoshiyuki; Iguchi, Nobuhiro; Yokota, Kiyoshi.
In: Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals, Vol. 39, No. 1, 01.1975, p. 24-28.Research output: Contribution to journal › Article
}
TY - JOUR
T1 - ON THE TRANSFORMATION IN EUTECTOID STEEL BY SUPER-RAPID HEATING.
AU - Miwa, Yoshiyuki
AU - Iguchi, Nobuhiro
AU - Yokota, Kiyoshi
PY - 1975/1
Y1 - 1975/1
N2 - In the previous paper the transformation temperature of pure iron by super-rapid heating was reported. In the present study the ( alpha plus Fe//3C yields gamma ) A//c//1 transformation behavior in eutectoid steel by super-rapid heating at 0 similar 10**7 degree C/sec was investigated using the same method as used for pure iron. The main results obtained are as follows: (1) The heating cycles up to the heating rate of 10**7 degree C/sec were recorded by the PbS cell heat-radiater and the dilatometer, from which the ( alpha plus Fe//3C yields gamma ) transformation temperature was determined. (2) The increment of the transformation point from the equilibrium point (A//c//1) in the eutectoid steel with heating rate (0 similar 10**7 degree C/sec) was determined. The A(clf) transformation curve is split up into two steps and in the lamellar pearlite specimen A(clf) was detected around 1100 degree C at the heating rate of 10**7 degree C/sec.
AB - In the previous paper the transformation temperature of pure iron by super-rapid heating was reported. In the present study the ( alpha plus Fe//3C yields gamma ) A//c//1 transformation behavior in eutectoid steel by super-rapid heating at 0 similar 10**7 degree C/sec was investigated using the same method as used for pure iron. The main results obtained are as follows: (1) The heating cycles up to the heating rate of 10**7 degree C/sec were recorded by the PbS cell heat-radiater and the dilatometer, from which the ( alpha plus Fe//3C yields gamma ) transformation temperature was determined. (2) The increment of the transformation point from the equilibrium point (A//c//1) in the eutectoid steel with heating rate (0 similar 10**7 degree C/sec) was determined. The A(clf) transformation curve is split up into two steps and in the lamellar pearlite specimen A(clf) was detected around 1100 degree C at the heating rate of 10**7 degree C/sec.
UR - http://www.scopus.com/inward/record.url?scp=0016424047&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0016424047&partnerID=8YFLogxK
M3 - Article
AN - SCOPUS:0016424047
VL - 39
SP - 24
EP - 28
JO - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
JF - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
SN - 0021-4876
IS - 1
ER -