Barium titanate (BaTiO3, BT) grain-oriented ceramics along  direction were prepared by a templated grain growth (TGG) method. The  oriented BT platelike particles (t-BT) were used as template particles. BT grain-oriented ceramics with higher relative density (Drel) over 95 %, high degree of orientation along  direction (F110) over 80 % and grain sizes around 30 μm were successfully prepared using only the template particles. The relationship between microstructures and piezoelectric constant (d33) was investigated. The higher F110 was, the higher Drel and the smaller grain size were required for enhancement of the piezoelectric properties.