Reliability-based durability design and service life assessment of reinforced concrete deck slab of jetty structures

Mitsuyoshi Akiyama, Dan M. Frangopol, Koshin Takenaka

    Research output: Contribution to journalArticle

    12 Citations (Scopus)

    Abstract

    Reinforced concrete (RC) structures in a marine environment deteriorate with time due to chloride-induced corrosion of reinforcing bars. Since the RC deck slabs of jetty structures are exposed to a very aggressive environment, higher deterioration rates can develop. In this paper, a reliability-based durability design and service life assessment of RC jetty structures are presented. For new RC jetty structures, the concrete quality and concrete cover necessary to prevent the chloride-induced reinforcement corrosion causing the deterioration of structural performance during the whole lifetime could be determined. Based on the airborne chloride hazard depending on the vertical distance from the sea level surface to the RC deck slab, the probability associated with the steel corrosion initiation is estimated. The water to cement ratio and concrete cover to satisfy the target reliability level are provided. For evaluating the service life of existing structures, the condition state based on the visual inspection of RC structure can be provided. The deterioration process of the RC jetty structure can be modelled as a Markov process. Therefore, the transition probability matrix at time t after construction can be updated by visual inspection results. A procedure to update the transition probability matrix by the Sequential Monte Carlo Simulation method is indicated. In an illustrative example, the effect of the updating on the life-cycle reliability estimate of existing RC deck slab in a jetty structure subjected to the chloride attack is presented.

    Original languageEnglish
    Pages (from-to)1-10
    Number of pages10
    JournalStructure and Infrastructure Engineering
    DOIs
    Publication statusAccepted/In press - 2016 Apr 7

    Fingerprint

    reinforced concrete
    durability
    Service life
    Reinforced concrete
    slab
    Durability
    concrete structure
    Concrete construction
    chloride
    Deterioration
    corrosion
    Concretes
    Inspection
    Corrosion
    Steel corrosion
    matrix
    services
    Sea level
    Markov processes
    reinforcement

    Keywords

    • chloride-induced corrosion
    • durability design
    • life-cycle
    • RC jetty structures
    • reliability
    • service life assessment
    • updating

    ASJC Scopus subject areas

    • Civil and Structural Engineering
    • Geotechnical Engineering and Engineering Geology
    • Safety, Risk, Reliability and Quality
    • Building and Construction
    • Mechanical Engineering
    • Ocean Engineering

    Cite this

    Reliability-based durability design and service life assessment of reinforced concrete deck slab of jetty structures. / Akiyama, Mitsuyoshi; Frangopol, Dan M.; Takenaka, Koshin.

    In: Structure and Infrastructure Engineering, 07.04.2016, p. 1-10.

    Research output: Contribution to journalArticle

    @article{54762a42d0df4dee9e0da77c0f28d11d,
    title = "Reliability-based durability design and service life assessment of reinforced concrete deck slab of jetty structures",
    abstract = "Reinforced concrete (RC) structures in a marine environment deteriorate with time due to chloride-induced corrosion of reinforcing bars. Since the RC deck slabs of jetty structures are exposed to a very aggressive environment, higher deterioration rates can develop. In this paper, a reliability-based durability design and service life assessment of RC jetty structures are presented. For new RC jetty structures, the concrete quality and concrete cover necessary to prevent the chloride-induced reinforcement corrosion causing the deterioration of structural performance during the whole lifetime could be determined. Based on the airborne chloride hazard depending on the vertical distance from the sea level surface to the RC deck slab, the probability associated with the steel corrosion initiation is estimated. The water to cement ratio and concrete cover to satisfy the target reliability level are provided. For evaluating the service life of existing structures, the condition state based on the visual inspection of RC structure can be provided. The deterioration process of the RC jetty structure can be modelled as a Markov process. Therefore, the transition probability matrix at time t after construction can be updated by visual inspection results. A procedure to update the transition probability matrix by the Sequential Monte Carlo Simulation method is indicated. In an illustrative example, the effect of the updating on the life-cycle reliability estimate of existing RC deck slab in a jetty structure subjected to the chloride attack is presented.",
    keywords = "chloride-induced corrosion, durability design, life-cycle, RC jetty structures, reliability, service life assessment, updating",
    author = "Mitsuyoshi Akiyama and Frangopol, {Dan M.} and Koshin Takenaka",
    year = "2016",
    month = "4",
    day = "7",
    doi = "10.1080/15732479.2016.1164725",
    language = "English",
    pages = "1--10",
    journal = "Structure and Infrastructure Engineering",
    issn = "1573-2479",
    publisher = "Taylor and Francis Ltd.",

    }

    TY - JOUR

    T1 - Reliability-based durability design and service life assessment of reinforced concrete deck slab of jetty structures

    AU - Akiyama, Mitsuyoshi

    AU - Frangopol, Dan M.

    AU - Takenaka, Koshin

    PY - 2016/4/7

    Y1 - 2016/4/7

    N2 - Reinforced concrete (RC) structures in a marine environment deteriorate with time due to chloride-induced corrosion of reinforcing bars. Since the RC deck slabs of jetty structures are exposed to a very aggressive environment, higher deterioration rates can develop. In this paper, a reliability-based durability design and service life assessment of RC jetty structures are presented. For new RC jetty structures, the concrete quality and concrete cover necessary to prevent the chloride-induced reinforcement corrosion causing the deterioration of structural performance during the whole lifetime could be determined. Based on the airborne chloride hazard depending on the vertical distance from the sea level surface to the RC deck slab, the probability associated with the steel corrosion initiation is estimated. The water to cement ratio and concrete cover to satisfy the target reliability level are provided. For evaluating the service life of existing structures, the condition state based on the visual inspection of RC structure can be provided. The deterioration process of the RC jetty structure can be modelled as a Markov process. Therefore, the transition probability matrix at time t after construction can be updated by visual inspection results. A procedure to update the transition probability matrix by the Sequential Monte Carlo Simulation method is indicated. In an illustrative example, the effect of the updating on the life-cycle reliability estimate of existing RC deck slab in a jetty structure subjected to the chloride attack is presented.

    AB - Reinforced concrete (RC) structures in a marine environment deteriorate with time due to chloride-induced corrosion of reinforcing bars. Since the RC deck slabs of jetty structures are exposed to a very aggressive environment, higher deterioration rates can develop. In this paper, a reliability-based durability design and service life assessment of RC jetty structures are presented. For new RC jetty structures, the concrete quality and concrete cover necessary to prevent the chloride-induced reinforcement corrosion causing the deterioration of structural performance during the whole lifetime could be determined. Based on the airborne chloride hazard depending on the vertical distance from the sea level surface to the RC deck slab, the probability associated with the steel corrosion initiation is estimated. The water to cement ratio and concrete cover to satisfy the target reliability level are provided. For evaluating the service life of existing structures, the condition state based on the visual inspection of RC structure can be provided. The deterioration process of the RC jetty structure can be modelled as a Markov process. Therefore, the transition probability matrix at time t after construction can be updated by visual inspection results. A procedure to update the transition probability matrix by the Sequential Monte Carlo Simulation method is indicated. In an illustrative example, the effect of the updating on the life-cycle reliability estimate of existing RC deck slab in a jetty structure subjected to the chloride attack is presented.

    KW - chloride-induced corrosion

    KW - durability design

    KW - life-cycle

    KW - RC jetty structures

    KW - reliability

    KW - service life assessment

    KW - updating

    UR - http://www.scopus.com/inward/record.url?scp=84963614853&partnerID=8YFLogxK

    UR - http://www.scopus.com/inward/citedby.url?scp=84963614853&partnerID=8YFLogxK

    U2 - 10.1080/15732479.2016.1164725

    DO - 10.1080/15732479.2016.1164725

    M3 - Article

    AN - SCOPUS:84963614853

    SP - 1

    EP - 10

    JO - Structure and Infrastructure Engineering

    JF - Structure and Infrastructure Engineering

    SN - 1573-2479

    ER -