Analysis of the segregated microstructures of electroless-deposited CoNiP perpendicular magnetic recording media using selective chemical etching

Takayuki Homma, K. Ohrui, Y. Iizuka, Tetsuya Osaka, Y. Yamazaki, T. Namikawa

研究成果: Article

抄録

The segregated microstructures of electroless-deposited CoNiP perpendicular magnetic recording media with various Hc(⊥) values-500, 1000 and 1500 Oe-were investigated using a selective chemical etching technique, in which Co-rich ferromagnetic regions were preferentially dissolved with an etchant of sodium hydroxide-m-nitrobenzenesulfonic acid-ethylenediamine aqueous solution. TEM observations of the etched 1500 Oe film revealed an 'asteroid' pattern with sixfold symmetry, which was inferred to be a substructure with Ni-rich composition. It is thought that the Co-rich regions are segregated between the 'arms' of the asteroid substructure. The shape of the substructure varied with the Hc(⊥) of the films; no substructure was observed in the 500 Oe film, while a substructure with a needlelike shape as well as a quasi-asteroid shape were observed in different regions of the 1000 Oe film. The differences in the segregation conditions are strongly dependent on the Hc(⊥) of the films. Further investigation of the 1500 Oe film in the thickness direction clearly indicated that the segregation occurs even in the initial deposition region (30 nm), and that the size of the substructure becomes larger with increasing film thickness.

元の言語English
ページ(範囲)853-857
ページ数5
ジャーナルIEEE translation journal on magnetics in Japan
8
発行部数12
DOI
出版物ステータスPublished - 1993 12

Fingerprint

Magnetic recording
Etching
Asteroids
Microstructure
Film thickness
Sodium
Transmission electron microscopy
Acids
Chemical analysis

ASJC Scopus subject areas

  • Engineering(all)

これを引用

@article{b77008c8091b42a59cc4265d885fbe9d,
title = "Analysis of the segregated microstructures of electroless-deposited CoNiP perpendicular magnetic recording media using selective chemical etching",
abstract = "The segregated microstructures of electroless-deposited CoNiP perpendicular magnetic recording media with various Hc(⊥) values-500, 1000 and 1500 Oe-were investigated using a selective chemical etching technique, in which Co-rich ferromagnetic regions were preferentially dissolved with an etchant of sodium hydroxide-m-nitrobenzenesulfonic acid-ethylenediamine aqueous solution. TEM observations of the etched 1500 Oe film revealed an 'asteroid' pattern with sixfold symmetry, which was inferred to be a substructure with Ni-rich composition. It is thought that the Co-rich regions are segregated between the 'arms' of the asteroid substructure. The shape of the substructure varied with the Hc(⊥) of the films; no substructure was observed in the 500 Oe film, while a substructure with a needlelike shape as well as a quasi-asteroid shape were observed in different regions of the 1000 Oe film. The differences in the segregation conditions are strongly dependent on the Hc(⊥) of the films. Further investigation of the 1500 Oe film in the thickness direction clearly indicated that the segregation occurs even in the initial deposition region (30 nm), and that the size of the substructure becomes larger with increasing film thickness.",
author = "Takayuki Homma and K. Ohrui and Y. Iizuka and Tetsuya Osaka and Y. Yamazaki and T. Namikawa",
year = "1993",
month = "12",
doi = "10.1109/TJMJ.1993.4565761",
language = "English",
volume = "8",
pages = "853--857",
journal = "IEEE translation journal on magnetics in Japan",
issn = "0882-4959",
number = "12",

}

TY - JOUR

T1 - Analysis of the segregated microstructures of electroless-deposited CoNiP perpendicular magnetic recording media using selective chemical etching

AU - Homma, Takayuki

AU - Ohrui, K.

AU - Iizuka, Y.

AU - Osaka, Tetsuya

AU - Yamazaki, Y.

AU - Namikawa, T.

PY - 1993/12

Y1 - 1993/12

N2 - The segregated microstructures of electroless-deposited CoNiP perpendicular magnetic recording media with various Hc(⊥) values-500, 1000 and 1500 Oe-were investigated using a selective chemical etching technique, in which Co-rich ferromagnetic regions were preferentially dissolved with an etchant of sodium hydroxide-m-nitrobenzenesulfonic acid-ethylenediamine aqueous solution. TEM observations of the etched 1500 Oe film revealed an 'asteroid' pattern with sixfold symmetry, which was inferred to be a substructure with Ni-rich composition. It is thought that the Co-rich regions are segregated between the 'arms' of the asteroid substructure. The shape of the substructure varied with the Hc(⊥) of the films; no substructure was observed in the 500 Oe film, while a substructure with a needlelike shape as well as a quasi-asteroid shape were observed in different regions of the 1000 Oe film. The differences in the segregation conditions are strongly dependent on the Hc(⊥) of the films. Further investigation of the 1500 Oe film in the thickness direction clearly indicated that the segregation occurs even in the initial deposition region (30 nm), and that the size of the substructure becomes larger with increasing film thickness.

AB - The segregated microstructures of electroless-deposited CoNiP perpendicular magnetic recording media with various Hc(⊥) values-500, 1000 and 1500 Oe-were investigated using a selective chemical etching technique, in which Co-rich ferromagnetic regions were preferentially dissolved with an etchant of sodium hydroxide-m-nitrobenzenesulfonic acid-ethylenediamine aqueous solution. TEM observations of the etched 1500 Oe film revealed an 'asteroid' pattern with sixfold symmetry, which was inferred to be a substructure with Ni-rich composition. It is thought that the Co-rich regions are segregated between the 'arms' of the asteroid substructure. The shape of the substructure varied with the Hc(⊥) of the films; no substructure was observed in the 500 Oe film, while a substructure with a needlelike shape as well as a quasi-asteroid shape were observed in different regions of the 1000 Oe film. The differences in the segregation conditions are strongly dependent on the Hc(⊥) of the films. Further investigation of the 1500 Oe film in the thickness direction clearly indicated that the segregation occurs even in the initial deposition region (30 nm), and that the size of the substructure becomes larger with increasing film thickness.

UR - http://www.scopus.com/inward/record.url?scp=0027741561&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0027741561&partnerID=8YFLogxK

U2 - 10.1109/TJMJ.1993.4565761

DO - 10.1109/TJMJ.1993.4565761

M3 - Article

AN - SCOPUS:0027741561

VL - 8

SP - 853

EP - 857

JO - IEEE translation journal on magnetics in Japan

JF - IEEE translation journal on magnetics in Japan

SN - 0882-4959

IS - 12

ER -