Atomic arrangement and formation of planar defects in the μ phase of Ni-base single crystal superalloys

Shiyu Ma, Xueqiao Li, Jianxin Zhang*, Jide Liu, Pan Li, Youjian Zhang, Huixin Jin, Wenyang Zhang, Yizhou Zhou, Xiaofeng Sun, Qing Zhang, Yanhui Chen, Shengcheng Mao

*この研究の対応する著者

研究成果: Article査読

11 被引用数 (Scopus)

抄録

The internal characteristics of the μ phase in Ni-base single crystal superalloys aged at 1100 °C for 1000 h were investigated via spherical aberration-corrected transmission electron microscopy. There were a large number of planar defects on the (001) plane at the growth tip of the μ phase. HAADF-STEM results show that these planar defects were mainly of two types. 1) A twin structure with a mirror plane of the middle atomic planes of the Zr4Al3 sheet, which was generated by shearing of atoms in the MgCu2 sheet along the [1-10] direction. 2) A mirror-symmetrical stacking fault of two Zr4Al3 sheets, which was formed by the pulling out of a single MgCu2 sheet. The planar defects were mainly caused by coordination of the distortions of the μ phase and the matrix. Segregation of Mo, Cr, and Re elements occurred near stacking faults, rather than twin structures.

本文言語English
ページ(範囲)775-783
ページ数9
ジャーナルJournal of Alloys and Compounds
766
DOI
出版ステータスPublished - 2018 10月 25
外部発表はい

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Atomic arrangement and formation of planar defects in the μ phase of Ni-base single crystal superalloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル