Beryllium implantation doping of silicon carbide

T. Henkel, Y. Tanaka, Naoto Kobayashi, S. Nishizawa, S. Hishita

研究成果: Chapter

抄録

Structural properties of beryllium implanted silicon carbide have been investigated by secondary ion mass spectrometry, Rutherford backscattering/channeling, and Raman spectroscopy. Strong redistribution of beryllium has been found after a post-implantation anneal step at temperatures between 1300 °C and 1700 °C. The use of a pre-anneal process at 1000 °C before the high-temperature treatment as well as graphite as a surface encapsulant do not efficiently suppress redistribution of Be in the SiC lattice. The crystalline state of the implanted and annealed material is well recovered after annealing at temperatures above 1400 °C.

元の言語English
ホスト出版物のタイトルMaterials Science Forum
出版者Trans Tech Publ Ltd
338
出版物ステータスPublished - 2000
外部発表Yes
イベントICSCRM '99: The International Conference on Silicon Carbide and Related Materials - Research Triangle Park, NC, USA
継続期間: 1999 10 101999 10 15

Other

OtherICSCRM '99: The International Conference on Silicon Carbide and Related Materials
Research Triangle Park, NC, USA
期間99/10/1099/10/15

Fingerprint

Beryllium
Silicon carbide
Ion implantation
Doping (additives)
Graphite
Rutherford backscattering spectroscopy
Secondary ion mass spectrometry
Crystal lattices
Temperature
Raman spectroscopy
Structural properties
Annealing
Crystalline materials
silicon carbide

ASJC Scopus subject areas

  • Materials Science(all)

これを引用

Henkel, T., Tanaka, Y., Kobayashi, N., Nishizawa, S., & Hishita, S. (2000). Beryllium implantation doping of silicon carbide. : Materials Science Forum (巻 338). Trans Tech Publ Ltd.

Beryllium implantation doping of silicon carbide. / Henkel, T.; Tanaka, Y.; Kobayashi, Naoto; Nishizawa, S.; Hishita, S.

Materials Science Forum. 巻 338 Trans Tech Publ Ltd, 2000.

研究成果: Chapter

Henkel, T, Tanaka, Y, Kobayashi, N, Nishizawa, S & Hishita, S 2000, Beryllium implantation doping of silicon carbide. : Materials Science Forum. 巻. 338, Trans Tech Publ Ltd, ICSCRM '99: The International Conference on Silicon Carbide and Related Materials, Research Triangle Park, NC, USA, 99/10/10.
Henkel T, Tanaka Y, Kobayashi N, Nishizawa S, Hishita S. Beryllium implantation doping of silicon carbide. : Materials Science Forum. 巻 338. Trans Tech Publ Ltd. 2000
Henkel, T. ; Tanaka, Y. ; Kobayashi, Naoto ; Nishizawa, S. ; Hishita, S. / Beryllium implantation doping of silicon carbide. Materials Science Forum. 巻 338 Trans Tech Publ Ltd, 2000.
@inbook{54584e442312442c931591df4e2bd1d7,
title = "Beryllium implantation doping of silicon carbide",
abstract = "Structural properties of beryllium implanted silicon carbide have been investigated by secondary ion mass spectrometry, Rutherford backscattering/channeling, and Raman spectroscopy. Strong redistribution of beryllium has been found after a post-implantation anneal step at temperatures between 1300 °C and 1700 °C. The use of a pre-anneal process at 1000 °C before the high-temperature treatment as well as graphite as a surface encapsulant do not efficiently suppress redistribution of Be in the SiC lattice. The crystalline state of the implanted and annealed material is well recovered after annealing at temperatures above 1400 °C.",
author = "T. Henkel and Y. Tanaka and Naoto Kobayashi and S. Nishizawa and S. Hishita",
year = "2000",
language = "English",
volume = "338",
booktitle = "Materials Science Forum",
publisher = "Trans Tech Publ Ltd",

}

TY - CHAP

T1 - Beryllium implantation doping of silicon carbide

AU - Henkel, T.

AU - Tanaka, Y.

AU - Kobayashi, Naoto

AU - Nishizawa, S.

AU - Hishita, S.

PY - 2000

Y1 - 2000

N2 - Structural properties of beryllium implanted silicon carbide have been investigated by secondary ion mass spectrometry, Rutherford backscattering/channeling, and Raman spectroscopy. Strong redistribution of beryllium has been found after a post-implantation anneal step at temperatures between 1300 °C and 1700 °C. The use of a pre-anneal process at 1000 °C before the high-temperature treatment as well as graphite as a surface encapsulant do not efficiently suppress redistribution of Be in the SiC lattice. The crystalline state of the implanted and annealed material is well recovered after annealing at temperatures above 1400 °C.

AB - Structural properties of beryllium implanted silicon carbide have been investigated by secondary ion mass spectrometry, Rutherford backscattering/channeling, and Raman spectroscopy. Strong redistribution of beryllium has been found after a post-implantation anneal step at temperatures between 1300 °C and 1700 °C. The use of a pre-anneal process at 1000 °C before the high-temperature treatment as well as graphite as a surface encapsulant do not efficiently suppress redistribution of Be in the SiC lattice. The crystalline state of the implanted and annealed material is well recovered after annealing at temperatures above 1400 °C.

UR - http://www.scopus.com/inward/record.url?scp=0033721925&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0033721925&partnerID=8YFLogxK

M3 - Chapter

AN - SCOPUS:0033721925

VL - 338

BT - Materials Science Forum

PB - Trans Tech Publ Ltd

ER -