Characteristics of photoelectrochemical cells with iron oxide/n-Si heterojunction photoanodes

Tetsuya Osaka*, Naruya Hirota, Taketoshi Hayashi, Svend Stensig Eskildsen

*この研究の対応する著者

研究成果: Article査読

11 被引用数 (Scopus)

抄録

The iron oxide/n-Si heterojunction electrode was studied as a photoanode for a regenerative photoelectrochemical (PEC) cell. The influence of modifying the top layer of the electrode with Pd or RuO2 was investigated. The photocurrent at the heterojunction electrode was produced by the holes which were photo-excited in both iron oxide and n-Si. The addition of Pd or RuO2 on the heterojunction electrode surface enhanced the optical-to-electrical conversion efficiency. The efficiencies for a stable working PEC cell were found to be 1.34% and 1.60% for a Pd-and a RuO2-modified electrode, respectively. This was measured in a 0.2 M KOH solution containing 0.2 M K4[Fe(CN)6] and 0.01 M K3[Fe(CN)6 at a xenon lamp intensity of 55 mW cm-2. The use of iron oxide made the photoanode highly stable, as compared to an electrode such as RuO2/n-Si. From a constant open-circuit voltage independent of the redox potential in 0.2 M KOH, it was concluded that Fermi level pinning occurs at the interface.

本文言語English
ページ(範囲)1209-1212
ページ数4
ジャーナルElectrochimica Acta
30
9
DOI
出版ステータスPublished - 1985 9

ASJC Scopus subject areas

  • 化学工学(全般)
  • 電気化学

フィンガープリント

「Characteristics of photoelectrochemical cells with iron oxide/n-Si heterojunction photoanodes」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル