Coercivity Recovery Effect of Sm-Fe-Cu-Al Alloy on Sm2Fe17N3 Magnet

Kohei Otogawa, Toru Asahi, Miho Jinno, Wataru Yamaguchi, Kenta Takagi*, Hansang Kwon

*この研究の対応する著者

    研究成果: Article査読

    1 被引用数 (Scopus)

    抄録

    The potential of a Sm-Fe-Cu-Al binder for improvement of the magnetic properties of Sm2Fe17N3 was examined. Transmission electron microscope (TEM) observation of a Sm-Fe-Cu-Al alloy-bonded Sm2Fe17N3 magnet which showed high coercivity revealed that the Sm-Fe-Cu-Al alloy had an effect of removing the surface oxide layer of the Sm2 Fe17N3 grains. However, the Sm-Fe-Cu-Al binder was contaminated by carbon and nitrogen, which originated from the organic solvent used as the milling medium during pulverization. To prevent carbon and nitrogen contamination, the Sm-Fe- Cu-Al alloy was added directly on the surface of the Sm2Fe17N3 grains by sputtering. Comparing the recovered coercivity per unit amount of the added binder the uncontaminated binder-coated sample had a higher coercivity recovery effect than the milled binder-added sample. These results suggested that sufficient addition of the contamination-free Sm-Fe-Cu-Al binder has the possibility to reduce the amount of binder necessary to produce a high coercive Sm2Fe17N3 magnet.

    本文言語English
    ページ(範囲)716-725
    ページ数10
    ジャーナルJournal of the Korean Physical Society
    72
    6
    DOI
    出版ステータスPublished - 2018 3 1

    ASJC Scopus subject areas

    • 物理学および天文学(全般)

    フィンガープリント

    「Coercivity Recovery Effect of Sm-Fe-Cu-Al Alloy on Sm<sub>2</sub>Fe<sub>17</sub>N<sub>3</sub> Magnet」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル