Comparison of dielectric properties between epoxy composites with nanosized clay fillers modified by primary amine and tertiary amine

N. Tagami*, M. Hyuga, Y. Ohki, T. Tanaka, T. Imai, M. Harada, M. Ochi

*この研究の対応する著者

研究成果: Article査読

60 被引用数 (Scopus)

抄録

Epoxy-based nanocomposites (NCs) were prepared using clay modified by either primary amine or tertiary amine, and the effect of the difference in modifier on the thermal and dielectric properties of the NCs were discussed. The NC with clay fillers modified by the primary amine, 1C, shows a glass transition end temperature (Teg) at a temperature 20 C lower than the neat epoxy (N). This indicates that the resin of 1C is less crosslinked than that of N. On the other hand, the sample 3C, in which the clay was modified by the tertiary amine, shows a DSC spectrum close to that of N. Namely, 3C has a high crosslinking density similar to N. While the three samples show a relaxation peak in their dielectric loss spectra, the peak appears at high frequencies in 1C compared to N and 3C. Moreover, ionic conduction current flows more at high temperatures in 1C than in N or 3C. These facts are ascribable to the difference in their crosslinking densities.

本文言語English
論文番号5412020
ページ(範囲)214-220
ページ数7
ジャーナルIEEE Transactions on Dielectrics and Electrical Insulation
17
1
DOI
出版ステータスPublished - 2010 2月

ASJC Scopus subject areas

  • 電子工学および電気工学

フィンガープリント

「Comparison of dielectric properties between epoxy composites with nanosized clay fillers modified by primary amine and tertiary amine」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル