Control of loading behavior of Y-type zeolite seeds on tubular alumina support

Masahiko Matsukata*, Taisuke Furuhata, Makoto Toyoda, Yasushi Sekine, Eiichi Kikuchi

*この研究の対応する著者

研究成果: Conference contribution

抄録

Zeolite membranes have often been prepared by the secondary growth method including dip-coating of zeolite seeds on the surface of porous support. Whereas the amount of seed crystals caught on the support surface would have critical influence of membrane formation, the dip-coating step itself and the effect of dip-coating on the quality of membrane have rarely been studied. In this study, we measured both zeta-potential of alumina support and Y-type zeolite seed slurry, and studied the effect of zeta-potential of them on the adhesion behavior of zeolite seeds on porous alumina support. Y-type zeolite seed-water slurry was prepared using ca. 200 nm of ultra stable Y crystals. The value of pH was controlled by adding NaOH or HCl solution. The concentration of zeolite slurry was controlled in the range of 1-5 g-zeolite/L. At lower pH, alumina support has positive charge, while zeolite seeds stayed at the isoelectric point. Under these conditions, zeolite seeds formed aggregated particles in size of ca. 6000 nm. Zeolite-water slurry was dip-coated on the surface of tubular porous alumina support with the average pore size of 0.15 μm. Thus, at lower pH, in the course of dip-coating procedure, zeolite seeds were exclusively trapped on the surface of porous tube. Hydrothermal treatment of seeded support was carried out to form a Y-type zeolite thin layer on the surface of tubular alumina support. The support seeded at lower pH value successfully gave a thin and compact layer of Y-type zeolite. The membrane prepared under such conditions showed a high perm selectivity to water in vapor permeation of isopropyl alcohol and water mixture.

本文言語English
ホスト出版物のタイトル11AIChE - 2011 AIChE Annual Meeting, Conference Proceedings
出版ステータスPublished - 2011 12月 1
イベント2011 AIChE Annual Meeting, 11AIChE - Minneapolis, MN, United States
継続期間: 2011 10月 162011 10月 21

出版物シリーズ

名前11AIChE - 2011 AIChE Annual Meeting, Conference Proceedings

Conference

Conference2011 AIChE Annual Meeting, 11AIChE
国/地域United States
CityMinneapolis, MN
Period11/10/1611/10/21

ASJC Scopus subject areas

  • 化学工学(全般)

フィンガープリント

「Control of loading behavior of Y-type zeolite seeds on tubular alumina support」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル