Corrosion behavior of a duplex stainless steel in a simulated crevice solution

So Aoki*, Reisuke Doi, Kiyotaka Ito, Jun'ichi Sakai, Hiroshi Yakuwa, Katsuhiro Mitsuhashi

*この研究の対応する著者

    研究成果: Conference contribution

    抄録

    The repassivation potential of corroding crevices of a duplex stainless steel was measured in a deaerated 3.5mass% NaCl solution according to JIS G 0592. The change of current density with time and preferential dissolution phase during anodic polarization in -370mV to +150mV (vs. SCE) potential region in a simulated crevice solution (25mass% NaCl, pH 0) were investigated. The repassivation potential of crevice corrosion depended on the holding potential and time for ensuring the propagation of crevice corrosion, and in all the cases, the preferential dissolution of ferritic phase was observed. The current density was rather steady during the potentiostatic measurement in the active peak region (-370mV to -260mV). While, it decreased with time in the active-passive transition region (-200mV to -150mV). In the passive region (0mV to +150mV), it first decreased, and then increased gradually. On the less-noble side of the active peak region, preferential dissolution occurred on the ferritic phase. On the other hand, on the noble side of the active peak region and in the active-passive transition region, it occurred on the austenitic phase. In the passive region, both phases dissolved evenly. These results suggest that the potential in the corroding crevice drops to the less-noble side of the active peak region by the IR drop mechanism.

    本文言語English
    ホスト出版物のタイトル17th International Corrosion Congress 2008: Corrosion Control in the Service of Society
    ページ927-935
    ページ数9
    2
    出版ステータスPublished - 2008
    イベント17th International Corrosion Congress 2008: Corrosion Control in the Service of Society - Las Vegas, NV
    継続期間: 2008 10 62008 10 10

    Other

    Other17th International Corrosion Congress 2008: Corrosion Control in the Service of Society
    CityLas Vegas, NV
    Period08/10/608/10/10

    ASJC Scopus subject areas

    • コロイド化学および表面化学
    • 表面、皮膜および薄膜

    フィンガープリント

    「Corrosion behavior of a duplex stainless steel in a simulated crevice solution」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル