Corrosion of Intermetallic Layer and Reliability of Au/Al Bonds

Tomohiro Uno*, Kohei Tatsumi

*この研究の対応する著者

研究成果: Article査読

9 被引用数 (Scopus)

抄録

In order to clarify the reliability on the mechanical and electrical properties of the bond between Au wire and Al thin pad, corrosion behavior of Au-Al intermetallic formed at the bond interface in the molding resin were investigated. The bonds were annealed at several elevated temperatures, T (423-573 K). Typical degradation was recognized by a decrease in bond strength as well as a remarkable increase in electrical resistance. The molding resin has great influence on the corrosion. Bi-phenyl (BP) epoxy resin was found to cause the degradation approximately six times faster than o-cresole novolac (OCN) epoxy. Activation energies of the bond failure were 1.5 eV (T>450 K) and 2.0 eV (7<450 K) in BP resin and 2.3 eV in OCN resin. The corroded part was revealed to be Au4Al intermetallic phase formed in the bond interface. The growth rate of corroded layer was proportional to annealing time t, which indicated the corrosion behavior was not diffusion-controlled. Activation energies of the growth rate of corroded layer in the BP and the OCN resin were 1.6 eV, 2.3 eV, respectively, which were very similar to those of the bond failure. The corrosion reaction of Au4Al and bromide produced minute Au precipitation (fcc) and Al oxide formation. The Al oxide was identified to be amorphous by EDS and electron diffraction.

本文言語English
ページ(範囲)406-415
ページ数10
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
63
3
DOI
出版ステータスPublished - 1999
外部発表はい

ASJC Scopus subject areas

  • 凝縮系物理学
  • 材料力学
  • 金属および合金
  • 材料化学

フィンガープリント

「Corrosion of Intermetallic Layer and Reliability of Au/Al Bonds」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル