Defect engineering for control of polarization properties in SrBi 2Ta2O9

Yuji Noguchi*, Masaru Miyayama, Kenichi Oikawa, Takashi Kamiyama, Minoru Osada, Masato Kakihana

*この研究の対応する著者

研究成果: Article査読

111 被引用数 (Scopus)

抄録

Defect engineering to design for remanent polarization (Pr) and coercive field (Ec) in SrBi2Ta2O9 (SBT) is proposed. Cation vacancies coupled with substituents or oxide vacancies are shown to play an essential role in determining the polarization properties. High-resolution neutron powder diffraction studies revealed that trivalent-cation (Bi, La, and Nd) substitution induces Sr vacancies for the requirement of charge neutrality. Polarization measurements of dense ceramics indicated that Bi substitution led to an increase in 2 Pr and the 2Pr value for Sr0.73Bi2.18 Ta2O 9 was twice as large as that of SBT. Structural refinements revealed that Bi substitution enhances spontaneous polarization (Ps) and the improvement of Ps is responsible for the larger 2Pr observed. La substitution with Sr vacancies increased Pr slightly, but the 2Ec value (41 kV/cm) of La0.33Sr 0.5Bi2Ta2O9 was much smaller than that for SBT (57 kV/cm). Nd-substituted SBT showed almost the same Pr of La-SBT, while a high 2Ec (125 kV/cm) was attained for Nd 0.33Sr0.5Bi2Ta2O9. It is suggested that the higher Ec found in Nd-SBT is attributed to oxide vacancies produced by the substitution of a very small amount of Nd at the Ta site. Defect engineering is expected to open the way for the design of the polarization properties in SBT

本文言語English
ページ(範囲)7062-7075
ページ数14
ジャーナルJapanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
41
11 B
DOI
出版ステータスPublished - 2002 11
外部発表はい

ASJC Scopus subject areas

  • 物理学および天文学(その他)

フィンガープリント

「Defect engineering for control of polarization properties in SrBi <sub>2</sub>Ta<sub>2</sub>O<sub>9</sub>」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル