Defect-free poly(9,9-bis(2-ethylhexyl)fluorene-2,7-vinylene) for polymer light-emitting diode (PLED) devices

Piched Auragudom*, Andrew A. Tangonan, Manoj A G Namboothiry, David L. Carroll, Rigoberto C. Advincula, Sukon Phanichphant, T. Randall Lee

*この研究の対応する著者

研究成果: Article査読

6 被引用数 (Scopus)

抄録

The π-conjugated light-emitting polymer poly (9,9-bis(2-ethylhexyl) fluorene-2,7-vinylene) (PEHFV) was synthesized in defect-free form via Horner-Emmons coupling. The structure and properties of the polymer were characterized by 1H NMR, 13C NMR, UV-vis, photoluminescence (PL), and electroluminescence (EL) spectroscopies as well as gel permeation chromatography (GPC) and thermogravimetric analysis (TGA). The weight-average molecular weight (Mw) and polydispersity of the PEHFV were 34,000 g/mol and 2.3, respectively. The UV-vis spectra showed absorption maxima at 425 and 452 nm, and the PL emission spectra showed a maximum at 505 nm with a shoulder at 541 nm. The polymer was soluble in common organic solvents and easily spin-coated on indium-tin oxide (ITO)-coated glass substrates. A doublelayer light-emitting device with an ITO/PEDOT:PSS/PFV/ Al configuration was fabricated. The turn-on voltage for the PEHFV device was observed at 3.0 V.

本文言語English
ページ(範囲)347-353
ページ数7
ジャーナルJournal of Polymer Research
17
3
DOI
出版ステータスPublished - 2010 5月
外部発表はい

ASJC Scopus subject areas

  • 材料化学
  • ポリマーおよびプラスチック
  • 有機化学

フィンガープリント

「Defect-free poly(9,9-bis(2-ethylhexyl)fluorene-2,7-vinylene) for polymer light-emitting diode (PLED) devices」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル