Deformation-resistant Ta0.2Hf0.8C solid-solution ceramic with superior flexural strength at 2000°C

Dmytro Demirskyi*, Hanna Borodianska, Toshiyuki Nishimura, Tohru S. Suzuki, Kyosuke Yoshimi, Oleg Vasylkiv

*この研究の対応する著者

研究成果査読

抄録

In this study, we explored the consolidation, solid-solution formation and high-temperature properties of tantalum hafnium carbide with the 1 TaC:4 HfC ratio, that is, Ta0.2Hf0.8C. Tantalum hafnium carbide bulks can be consolidated using spark-plasma sintering only at temperatures exceeding 2200°C. The bulks prepared using a 40-min dwell at 2200°C had the lattice parameter a = 4.571(9) Å. Based on the three-point flexural tests, it was observed that the toughness and strength of Ta0.2Hf0.8C remained high at 2000°C (3.4 ± 0.4 MPa m1/2, 500 ± 20 MPa). At 2000°C, majority of carbides show a plastic behavior, but the strain-stress curves of the SPSed Ta0.2Hf0.8C ceramic were linear. Using the shrinkage rate data during the SPS and the strain-stress data from the high-temperature flexure, we estimated the activation energies for the densification and flexure as 820 ± 20 kJ/mol and 1180 ± 120 kJ/mol, respectively.

本文言語English
ページ(範囲)512-524
ページ数13
ジャーナルJournal of the American Ceramic Society
105
1
DOI
出版ステータスPublished - 2022 1
外部発表はい

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 材料化学

フィンガープリント

「Deformation-resistant Ta<sub>0.2</sub>Hf<sub>0.8</sub>C solid-solution ceramic with superior flexural strength at 2000°C」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル