Degradation mechanisms of silicone rubber under different aging conditions

Takuya Kaneko, Seitaro Ito, Takefumi Minakawa, Naoshi Hirai, Yoshimichi Ohki

研究成果: Article査読

16 被引用数 (Scopus)

抄録

Various kinds of aging treatments were given to silicone rubber (SiR), an important inorganic polymer for electrical insulation. Then, the SiR sheets were examined by terahertz (THz) absorption spectroscopy, infrared absorption spectroscopy, nuclear magnetic resonance, and indenter modulus. As a result, it has become clear that three degradation mechanisms appear in SiR, depending on the aging condition. If SiR is aged thermally, the formation of cross-linked structures dominates. On the other hand, the oxidation of cyclic siloxane at the surface appears obviously if SiR is gamma irradiated at room temperature. In the case of steam exposure at 155 °C, SiR loses its molecular weight by hydrolysis. Corresponding with these aging processes, specific changes appear in THz absorption spectra. Regarding this, THz absorption spectroscopy is useable for condition-monitoring of SiR.

本文言語English
論文番号108936
ジャーナルPolymer Degradation and Stability
168
DOI
出版ステータスPublished - 2019 10

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Polymers and Plastics
  • Materials Chemistry

フィンガープリント 「Degradation mechanisms of silicone rubber under different aging conditions」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル