Degradation of Flame-retardant Cross-linked Polyolefin Aged by Heat and Radiation

Haolong Zhou, Wakana Hanafusa, Keigo Udo, Naoshi Hirai, Yoshimichi Ohki

研究成果: Conference contribution

抄録

For investigating the degradation mechanism of flame-retardant cross-linked polyolefin (FR-XLPO), sheets of FR-XLPO were aged thermally with and without co-irradiation of gamma rays. As a result of the analysis conducted thermally and electrically, FR-XLPO was found to be degraded severer when it is aged purely thermally than when aged with the co-irradiation of gamma rays. It seems that FR-XLPO becomes more resistive against the degradation and the following bond scission by the formation of slightly cross-linked structures.

本文言語English
ホスト出版物のタイトル7th IEEE International Conference on High Voltage Engineering and Application, ICHVE 2020 - Proceedings
出版社Institute of Electrical and Electronics Engineers Inc.
ISBN(電子版)9781728155111
DOI
出版ステータスPublished - 2020 9 6
イベント7th IEEE International Conference on High Voltage Engineering and Application, ICHVE 2020 - Beijing, China
継続期間: 2020 9 62020 9 10

出版物シリーズ

名前7th IEEE International Conference on High Voltage Engineering and Application, ICHVE 2020 - Proceedings

Conference

Conference7th IEEE International Conference on High Voltage Engineering and Application, ICHVE 2020
CountryChina
CityBeijing
Period20/9/620/9/10

ASJC Scopus subject areas

  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering
  • Mechanics of Materials
  • Safety, Risk, Reliability and Quality
  • Electronic, Optical and Magnetic Materials

フィンガープリント 「Degradation of Flame-retardant Cross-linked Polyolefin Aged by Heat and Radiation」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル