Denser and taller carbon nanotube arrays on Cu foils useable as thermal interface materials

Nuri Na, Kei Hasegawa, Xiaosong Zhou, Mizuhisa Nihei, Suguru Noda

研究成果: Article

7 引用 (Scopus)

抜粋

To achieve denser and taller carbon nanotube (CNT) arrays on Cu foils, catalyst and chemical vapor deposition (CVD) conditions were carefully engineered. CNTs were grown to ∼50μm using Fe/TiN/Ta catalysts in which Ta and TiN acted as diffusion barriers for Cu and Ta, respectively. A tradeoff was found between the mass density and height of the CNTarrays, and CNTarrays with a mass density of 0.30 g cm-3 and height of 45μm were achieved under optimized conditions. Thermal interface materials (TIMs) with CNT array/Cu foil/CNT array structures showed decreasing thermal resistance from 86 to 24mm2KW-1 with increasing CNT array mass densities from 0.07-0.08 to 0.19-0.26 g cm-3 for Cu and Al blocks with surfaces as rough as 20-30 μm. The best CNT/Cu/CNT TIMs showed thermal resistance values comparable to that of a typical indium sheet TIM.

元の言語English
記事番号095102
ジャーナルJapanese journal of applied physics
54
発行部数9
DOI
出版物ステータスPublished - 2015 9 1

    フィンガープリント

ASJC Scopus subject areas

  • Engineering(all)
  • Physics and Astronomy(all)

これを引用