Densification and superplasticity of hydroxyapatite ceramics

Keiichiro Tago, Kiyoshi Itatani, Tohru S. Suzuki, Yoshio Sakka, Seiichiro Koda

研究成果: Article

19 引用 (Scopus)

抜粋

Fabrication conditions for high-density and fine-grained hydroxyapatite (Ca10 (PO4)6(OH)2: HAp) ceramic were examined; the tensile elongation of HAp ceramic during heating was measured in order to evaluate its possible superplastic behavior. The HAp compact was fired in air at a temperature between 1100 and 1200°C for 5 h. The relative density of HAp compact fired at 1100°C for 5 h showed a maximum (99.2%), whereas the average grain size was as small as 0.56 μm. The tensile elongation of this HAp specimen was tested at a temperature between 940 and 1100°C. The tensile elongations tested at 1050 and 1100°C attained 156 and 157%, respectively; the specimen tested at 1050°C contained a limited number of cavities, whereas the specimen tested at 1100°C was observed to have a large number of cavities.

元の言語English
ページ(範囲)669-673
ページ数5
ジャーナルJournal of the Ceramic Society of Japan
113
発行部数1322
DOI
出版物ステータスPublished - 2005 10
外部発表Yes

ASJC Scopus subject areas

  • Ceramics and Composites
  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry

フィンガープリント Densification and superplasticity of hydroxyapatite ceramics' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用