Desorption behaviours from metal-N-H systems synthesized by ball milling

H. Y. Leng, T. Ichikawa, S. Isobe, S. Hino, N. Hanada, H. Fujii

研究成果: Article査読

68 被引用数 (Scopus)

抄録

Three metal amides LiNH2, NaNH2 and Mg(NH 2)2 were synthesized by ball milling the metal hydrides under gaseous ammonia NH3 at room temperature. The decomposition behaviours from these metal amides were investigated by thermal desorption mass spectroscopy and thermogravimetry analysis methods. The results showed that LiNH2 decomposed at T>230° C and was transformed into the imide Li2NH with emitting NH3, while Mg(NH 2)2, decomposed at T>180° C and was transformed into MgNH and finally into Mg3N2 with emitting NH 3 within 500 ° C. Then, a new metal-N-H system composed of Mg(NH2)2 and LiH with a molar ratio of 3:8 was designed by ball milling treatment and examined the hydrogen storage properties. The results showed that this system could reversibly absorb/desorb a large amount of hydrogen (∼ 7 wt.%) at a moderate temperature and pressure, which was better than the system of LiNH2 and LiH for hydrigen storage.

本文言語English
ページ(範囲)443-447
ページ数5
ジャーナルJournal of Alloys and Compounds
404-406
SPEC. ISS.
DOI
出版ステータスPublished - 2005 12 8
外部発表はい

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Desorption behaviours from metal-N-H systems synthesized by ball milling」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル