Detection of solidification cracking of Al-7mass%Si alloy by using acoustic emission and visualization methods

Itaru Endo, Hiroyuki Chiba, Toru Ueki, Takanari Toriyama, Makoto Yoshida

研究成果: Article

抜粋

Detection of AE signals of solidification cracking of Al-7mass%Si alloy was attempted with in situ microscopic observation on the surface of casting using high speed camera. During solidification, it was found that AE signal from the casting with crack was higher than AE signal from the casting without crack. As a result of observation of casting using high speed camera, it was found that a rise of AE signal corresponded to initiation of solidification cracking. This stage was the stage of eutectic solidification. Thus, AE signals of solidification cracking should be generated during eutectic solidification. However, AE signals from the casting without cracking were also detected during solidification. This means that AE signals other than solidification cracking should be generated during solidification. Therefore, AE signals detected during eutectic solidification is not necessarily AE signals of solidification cracking. In order to detect AE signals of solidification cracking, it is necessary to separate AE signals of solidification cracking and other than solidification cracking.

元の言語English
ページ(範囲)486-491
ページ数6
ジャーナルKeikinzoku/Journal of Japan Institute of Light Metals
60
発行部数10
DOI
出版物ステータスPublished - 2010 12 1

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント Detection of solidification cracking of Al-7mass%Si alloy by using acoustic emission and visualization methods' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用