Distribution of cobalt between MgO-saturated FeOx-MgO-CaO- SiO2 Slag and Fe-Cu-Co molten alloy

Shin Ya Kitamura, Hideki Kuriyama, Nobuhiro Maruoka, Katsunori Yamaguchi, Akira Hasegawa

研究成果: Article

3 引用 (Scopus)

抜粋

During the decommissioning phase of a nuclear reactor, most of the steel-reinforced concrete shielding around a pressure vessel is considered as low-level radioactive waste. It is highly desirable to reduce the radioactivity level of this waste to below the clearance level. Normally, the radioactivity of steel after irradiation is found to be proportional to the cobalt content. In this study, for the production of low-activation steel in steelmaking process. cobalt distribution between MgO-saturated FeOx-MgO-CaO-Si0 2 slag and Fe-Cu-Co molten alloy was investigated. The results are summarized as follows: (1) the distribution ratio increases with decreasing temperature and (2) the activity coefficient of CoO decreases with increasing temperature and decreasing slag basicity. Although low temperature and low basicity are suitable conditions for refining, it is extremely difficult to decrease the Co content by an oxidation reaction. because of a very small distribution ratio of cobalt.

元の言語English
ページ(範囲)2636-2641
ページ数6
ジャーナルMaterials Transactions
49
発行部数11
DOI
出版物ステータスPublished - 2008 11 1
外部発表Yes

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Distribution of cobalt between MgO-saturated FeO<sub>x</sub>-MgO-CaO- SiO<sub>2</sub> Slag and Fe-Cu-Co molten alloy' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用