Duplex Structure and Crystallization of Anodic Alumina Films

O. N.O. Sachiko*, Tetsuya Osaka, Noboru Masuko

*この研究の対応する著者

研究成果: Article査読

9 被引用数 (Scopus)

抄録

The structure and the formation behavior of crystalline anodic films formed on aluminum in the mixture of boric acid / ammonium borate solution have been investigated. The film is composed of a boron-containing outer layer and a boron-free inner layer with lens-like crystals being present at the interface. The transport number of A13+ estimated from the thickness ratio of the outer to inner layers is 0.4 when the film is formed at the current density of 20 A-m'2 It increases to 0.45 when the current density is 200 A-m'2. The film thickness decreases with increasing current density. A porous cell structure is developed when the film is formed at a current density higher than 100 A-m"2. Voids in the lens-like crystals are localized in three different regions; i.e., the center top region, the upper interface region between amorphous and crystalline phases, and the lower half region of the crystals.

本文言語English
ページ(範囲)819-824
ページ数6
ジャーナルDenki Kagaku
64
7
DOI
出版ステータスPublished - 1996

ASJC Scopus subject areas

  • 化学 (全般)

フィンガープリント

「Duplex Structure and Crystallization of Anodic Alumina Films」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル