Effect of Notch Root Radius on Fracture of Glass/Epoxy Laminates (under Tensile Loading)

Hiroyuki Kawada, Ikuhiko Hayashi, Takehiko Hosoi, Jiro Hiramoto

研究成果査読

抄録

Tensile tests were conducted on specimens of plain woven glass cloth/epoxy laminates with a notch. The effect of the notch root radius p on fracture was investigated. In the previous study, the three-point bending tests were carried out to make clear the effect of the notch root radius on fracture. In this study, the experimental results were compared with those of the previous study. The F. E. M. simulation was performed, and compared with the experimental results. The following results were obtained: (1) As the notch root radius increased, the smaller p specimen showed the fracture behavior which was caused mainly by the propagation of a stable crack, but the larger p specimen showed the fracture behavior which was caused mainly by the spread of the damage. (2) The spread of the damage zone was different from that of the three-point bending test, but the effect of the notch root radius on strength remained unchanged for the tension and the bending test. (3) The F. E. M simulation explained the experimental result of the larger p specimen well.

本文言語English
ページ(範囲)390-396
ページ数7
ジャーナルZairyo/Journal of the Society of Materials Science, Japan
36
403
DOI
出版ステータスPublished - 1987

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Effect of Notch Root Radius on Fracture of Glass/Epoxy Laminates (under Tensile Loading)」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル