EFFECT OF STACKING FAULT PRECIPITATION ON HOT DEFORMATION OF AUSTENITIC STAINLESS STEEL.

Kazuhito Kamei, Yasuhiro Maehara, Yasuya Ohmori

研究成果: Article査読

3 被引用数 (Scopus)

抄録

Hot deformation characteristics of Nb-bearing austenitic stainless steel have been studied 823 to 1173 K at an initial strain rate of 2. 1 multiplied by 10** minus **4 s** minus **1. Although yield strength of the solution-treated specimen was low, work hardening occured at 1023 to 1123 K. A ductility trough accompanied by intergranular ductile fracture was also observed. In the aged specimen, yield strength was higher but work hardening was less significant, probably due to refinement of the average effective grain size. At temperature above 1123 K, ductility of the solution-treated speciment increased with temperature but that of the aged specimen was reduced. Ductility loss could arise from local dynamic recrystallization in the vicinity of grain boundaries.

本文言語English
ページ(範囲)159-166
ページ数8
ジャーナルTransactions of the Iron and Steel Institute of Japan
26
2
出版ステータスPublished - 1986
外部発表はい

ASJC Scopus subject areas

  • Engineering(all)

フィンガープリント 「EFFECT OF STACKING FAULT PRECIPITATION ON HOT DEFORMATION OF AUSTENITIC STAINLESS STEEL.」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル