Effect of twinning and aging treatment on fatigue process of ZK60 magnesium alloys

Shunsuke Taniguchi, Rumi Kitazawa, Yoshihisa Tanaka, Makoto Yoshida, Susumu Horibe

研究成果: Article査読

抄録

For magnesium alloy ZK60 with different heat treatments, controlled plastic strain amplitude fatigue tests were conducted. Effects of twinning and aging treatments on fatigue process were investigated by analyzing the second derivative of hysteresis half-loop. It is found that during compression the convex peak appears at the strain where twinning begins. It is also found that during tension the convex peak appears at the strain where detwinning begins and the concave peak appears at the strain where slip begins to be predominant. Analyzing the strain at the convex peak in compression at the plastic strain amplitude of 6 × 10-3, for solution treated material and over-aged material twinning hardens with increasing cycle. On the other hand, for T6 material twinning softens from 5 cycle to Nf/5 cycle and then hardens from Nf/5 cycle to Nf/2 cycle. It was suggested that residual twins cause twinning hardening. It was also suggested that cut and dissolution of rod-like precipitates should cause twinning softening. Due to different states of precipitates of materials, the twinning softening appeared for only T6 material at the plastic strain amplitude of 6 × 10 -3. Moreover, the softening were not found for T6 material under the plastic strain amplitude of 4 × 10-3.

本文言語English
ページ(範囲)448-454
ページ数7
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
77
10
DOI
出版ステータスPublished - 2013 10

ASJC Scopus subject areas

  • 凝縮系物理学
  • 材料力学
  • 金属および合金
  • 材料化学

フィンガープリント

「Effect of twinning and aging treatment on fatigue process of ZK60 magnesium alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル