Effects of microstructure on the subsurface crack initiation of Ti-6Al-4V alloys

O. Umezawa*, K. Nagai, H. Yokoyama, T. Suzuki

*この研究の対応する著者

研究成果: Paper査読

5 被引用数 (Scopus)

抄録

In order to clarify how the subsurface crack initiation site generates according to microstructure in high-cycle fatigue, Ti-6Al-4V alloys with different microstructures were subjected to fatigue test in liquid nitrogen. Microstructure influenced the S-N curves in long-life range. The subsurface crack initiation site was a facet or its aggregate which originated from the α grain transgranular cracking in each material. The size of subsurface crack initiation site highly depended on the maximum cyclic stress range.

本文言語English
ページ287-298
ページ数12
出版ステータスPublished - 1997 12月 1
外部発表はい
イベントProceedings of the 1997 TMS Fall Symposium - Indianapolis, IN, USA
継続期間: 1997 9月 141997 9月 18

Conference

ConferenceProceedings of the 1997 TMS Fall Symposium
CityIndianapolis, IN, USA
Period97/9/1497/9/18

ASJC Scopus subject areas

  • 工学(全般)

フィンガープリント

「Effects of microstructure on the subsurface crack initiation of Ti-6Al-4V alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル