Effects of Thickness and Specimen Size on Fracture Toughness of Glass/Epoxy Laminates

Hiroyuki Kawada, Toshihiro Otsuka

研究成果: Article査読

抄録

Three points bending tests were conducted on specimens of plain woven glass cloth/epoxy laminates (fiber volume fraction%0.4) with notch and R curves were obtained. The effects of the thickness and the size of the specimens on the fracture toughness were investigated. The crack propagation was experimentally observed with the ink method. The electric potential method and the acoustic emission method were carried out to detect the initiation of the crack. In this study, the validity of these nondestructive inspection method was examined corresponding to the loaddisplacement curves. The following results were obtained: (1) the effect of the thickness on the fracture toughness was less than that of the specimen size, (2) the outputs in the electric potential method were correlatable with the initiation of the damage and the propagation of macroscopic crack, and classified into three distinct patterns and (3) AE counts gave so much information for the fracture behavior in such a way that the initiation of the damage and the proportional limit corresponded to the initiation and the rapid increase of the AE event counts, respectively.

本文言語English
ページ(範囲)164-170
ページ数7
ジャーナルJournal of the Society of Materials Science, Japan
34
377
DOI
出版ステータスPublished - 1985 1月 1

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Effects of Thickness and Specimen Size on Fracture Toughness of Glass/Epoxy Laminates」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル