Effects of TiC Addition on Directionally Solidified Microstructure of Ti6Al4V

Shunya Yamamoto*, Naoki Date, Yuhi Mori, Shinsuke Suzuki, Yoshimi Watanabe, Shizuka Nakano, Naoko Sato

*この研究の対応する著者

研究成果: Article査読

1 被引用数 (Scopus)

抄録

In this study, the effects of TiC particles as the heterogeneous nucleus on the microstructure of directionally solidified Ti6Al4V were investigated. Ti6Al4V powder containing 0.0, 0.3, 1.0, and 2.0 vol pct TiC particles in a Ti6Al4V sheath was melted and directionally solidified with a floating zone melting method. In this process, the temperature gradient G was approximately 12 K/mm, and the solidification rate R was 15 mm/min. The mean size of prior β grains decreased with increasing TiC addition. In samples containing TiC particles, some grains had an aspect ratio lower than 1. This indicated that TiC particles acted as the heterogeneous nucleus and generated fine and equiaxed prior β grains. Although the many TiC particles melted into molten Ti6Al4V and the excessively melted carbon from TiC particles precipitated as Ti2C, residual TiC particles acted as a heterogeneous nucleus.

本文言語English
ページ(範囲)3174-3185
ページ数12
ジャーナルMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
50
7
DOI
出版ステータスPublished - 2019 7 15

ASJC Scopus subject areas

  • 凝縮系物理学
  • 材料力学
  • 金属および合金

フィンガープリント

「Effects of TiC Addition on Directionally Solidified Microstructure of Ti6Al4V」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル