Elemental effects on the oxidation of refractory compositionally complex alloys

Kai Chi Lo*, Hideyuki Murakami, Uwe Glatzel, Jien Wei Yeh, Stéphane Gorsse, An Chou Yeh


研究成果: Article査読


The oxidation of refractory compositionally complex alloys (RCCAs) is one of the most critical subjects for their high temperature applications. In this work, several RCCAs were systematically designed and isothermally oxidised at 1000 °C for up to 24 h; the elemental effects of Al, Cr, Mo, Nb Ta, Ti, V, and Zr on the oxidation of the RCCAs were studied. It was found that Al, Cr, Ti could enhance the oxidation resistance of the RCCAs by promoting the formation of rutile-type AlTaO4, CrTaO4, and their related oxides, while Zr and V formed non-protective oxides such as Nb2Zr6O17, Ta2Zr6O17, ZrTiO4, and VTa9O25, resulting in severe internal oxidation. Mo appeared to be effective in suppressing internal oxidation, but it could form non-protective MoTiTa8O25. Ta was slightly more beneficial than Nb for reducing the oxidation mass gain. This study provides insights on the elemental effects on the oxidation and guidelines for improving the oxidation resistance of RCCAs.

ジャーナルInternational Journal of Refractory Metals and Hard Materials
出版ステータスPublished - 2022 11月

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学


「Elemental effects on the oxidation of refractory compositionally complex alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。