Elucidation of structure and conduction mechanism in Nd-Mn substituted Y-type strontium hexaferrites

Bashir Ahmad, Muhammad Naeem Ashiq*, Muhammad Shuaib Khan, Minoru Osada, Muhammad Najam-Ul-Haq, Irshad Ali

*この研究の対応する著者

    研究成果: Article査読

    12 被引用数 (Scopus)

    抄録

    Technologically important ferrites magnetic materials with nominal composition “Sr2-xNdxCo2MnyFe12-yO22” (x = 0.0 to 0.1 and y = 0.0 to 1.0) were fabricated by the simple sol-gel method. The X-ray diffraction analysis endorsed the formation of well-defined Y-type hexagonal single phase with crystallite size in range of 38–45 nm. Owing to reduction of Fe3+ ions at octahedral site, an increase in DC resistivity was observed from 4.083 × 108 to 2.376 × 109 Ω-cm with the increase in substituents content. The two conduction mechanisms operating in ferri- and paramagnetic regions were shown by Arrhenius plot. It was observed that conduction in ferrimagnetic and paramagnetic regions was governed by the hopping of electrons and polarons, respectively. The decrease in Curie temperature “Tc” (553-423 K) was detected as a factor of Nd-Mn content due to decrease in Fe[sbnd]Fe interaction at octahedral site. The changes in the values of dielectric constant (ε), dielectric loss factor (ε) and tan loss (δ) follow Maxwell-Wagner model. The relatively high resistivity (2.376 × 109 Ω-cm) and low dielectric constants (2.97 at 1 MHz) for the sample with x = 0.1 and y = 1.0 make this material as an excellent candidates for high frequency microwave devices.

    本文言語English
    ページ(範囲)9-16
    ページ数8
    ジャーナルJournal of Alloys and Compounds
    723
    DOI
    出版ステータスPublished - 2017 11月 5

    ASJC Scopus subject areas

    • 材料力学
    • 機械工学
    • 金属および合金
    • 材料化学

    フィンガープリント

    「Elucidation of structure and conduction mechanism in Nd-Mn substituted Y-type strontium hexaferrites」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル