Fabrication and mechanical properties of Lotus-type porous carbon steel by unidirectional solidification in nitrogen atmosphere

Makoto Kashihara; Hirosi Yonetani; Takahiro Kobi; Soong Keun Hyun; Shinsuke Suzuki; Hideo Nakajima

doi:10.2355/tetsutohagane.94.30

Fabrication and mechanical properties of Lotus-type porous carbon steel by unidirectional solidification in nitrogen atmosphere

Makoto Kashihara^*, Hirosi Yonetani, Takahiro Kobi, Soong Keun Hyun, Shinsuke Suzuki, Hideo Nakajima

^*この研究の対応する著者

研究成果: Article › 査読

3 被引用数 (Scopus)

抄録

Lotus-type porous carbon steel (AISI 1018) whose long cylindrical pores are aligned in one direction was fabricated by unidirectional solidification in pressurized nitrogen gas. The ingots with the porosity from 10 to 30% were fabricated under the nitrogen gas pressure of 2.5 MPa at various transference velocities from 40 to 160 ,μm s^-1. Tensile strength was measured for Lotus-type porous carbon steel. Elongation was improved due to normalizing at 1200K. The yield strength does not change even in lotus steel less than 20% in porosity. This superior property is attributed to nitrogen solid solution hardening and pore existence.

本文言語	English
ページ（範囲）	30-34
ページ数	5
ジャーナル	Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
巻	94
号	1
DOI	https://doi.org/10.2355/tetsutohagane.94.30
出版ステータス	Published - 2008
外部発表	はい

ASJC Scopus subject areas

凝縮系物理学
物理化学および理論化学
金属および合金
材料化学

文献へのアクセス

10.2355/tetsutohagane.94.30

他のファイルとリンク

フィンガープリント

「Fabrication and mechanical properties of Lotus-type porous carbon steel by unidirectional solidification in nitrogen atmosphere」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル

@article{737cf564434847bc8a72b799d9539f7d,

title = "Fabrication and mechanical properties of Lotus-type porous carbon steel by unidirectional solidification in nitrogen atmosphere",

abstract = "Lotus-type porous carbon steel (AISI 1018) whose long cylindrical pores are aligned in one direction was fabricated by unidirectional solidification in pressurized nitrogen gas. The ingots with the porosity from 10 to 30% were fabricated under the nitrogen gas pressure of 2.5 MPa at various transference velocities from 40 to 160 ,μm s-1. Tensile strength was measured for Lotus-type porous carbon steel. Elongation was improved due to normalizing at 1200K. The yield strength does not change even in lotus steel less than 20% in porosity. This superior property is attributed to nitrogen solid solution hardening and pore existence.",

keywords = "Lotus-type porous carbon steel, Nitrogen, Porosity, Porous metals, Tensile test, Unidirectional solidification",

author = "Makoto Kashihara and Hirosi Yonetani and Takahiro Kobi and Hyun, {Soong Keun} and Shinsuke Suzuki and Hideo Nakajima",

year = "2008",

doi = "10.2355/tetsutohagane.94.30",

language = "English",

volume = "94",

pages = "30--34",

journal = "Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan",

issn = "0021-1575",

publisher = "Iron and Steel Institute of Japan",

number = "1",

}

TY - JOUR

T1 - Fabrication and mechanical properties of Lotus-type porous carbon steel by unidirectional solidification in nitrogen atmosphere

AU - Kashihara, Makoto

AU - Yonetani, Hirosi

AU - Kobi, Takahiro

AU - Hyun, Soong Keun

AU - Suzuki, Shinsuke

AU - Nakajima, Hideo

PY - 2008

Y1 - 2008

N2 - Lotus-type porous carbon steel (AISI 1018) whose long cylindrical pores are aligned in one direction was fabricated by unidirectional solidification in pressurized nitrogen gas. The ingots with the porosity from 10 to 30% were fabricated under the nitrogen gas pressure of 2.5 MPa at various transference velocities from 40 to 160 ,μm s-1. Tensile strength was measured for Lotus-type porous carbon steel. Elongation was improved due to normalizing at 1200K. The yield strength does not change even in lotus steel less than 20% in porosity. This superior property is attributed to nitrogen solid solution hardening and pore existence.

AB - Lotus-type porous carbon steel (AISI 1018) whose long cylindrical pores are aligned in one direction was fabricated by unidirectional solidification in pressurized nitrogen gas. The ingots with the porosity from 10 to 30% were fabricated under the nitrogen gas pressure of 2.5 MPa at various transference velocities from 40 to 160 ,μm s-1. Tensile strength was measured for Lotus-type porous carbon steel. Elongation was improved due to normalizing at 1200K. The yield strength does not change even in lotus steel less than 20% in porosity. This superior property is attributed to nitrogen solid solution hardening and pore existence.

KW - Lotus-type porous carbon steel

KW - Nitrogen

KW - Porosity

KW - Porous metals

KW - Tensile test

KW - Unidirectional solidification

UR - http://www.scopus.com/inward/record.url?scp=67650804879&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=67650804879&partnerID=8YFLogxK

U2 - 10.2355/tetsutohagane.94.30

DO - 10.2355/tetsutohagane.94.30

M3 - Article

AN - SCOPUS:67650804879

SN - 0021-1575

VL - 94

SP - 30

EP - 34

JO - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

JF - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

IS - 1

ER -