Fabrication and mechanical properties of textured Ti3SiC2 systems using commercial powder

Yuichi Uchida, Koji Morita, Tohru S. Suzuki, Toshiyuki Nishimura, Kenjiro Fujimoto, Yoshio Sakka

研究成果: Article査読

1 被引用数 (Scopus)

抄録

Ti3SiC2 is a typical Mn+1AXn (MAX) phase ceramic and exhibits both metal-like and ceramic-like properties. To improve these properties, texturing and Al2O3 addition were performed. The commercial Ti3SiC2 powder used contained approximately 10 mass% TiC phase. Textured Ti3SiC2 was prepared by slip casting in a strong magnetic field (MF) followed by spark plasma sintering (SPS) at 1623 K under a pressure of 40 MPa for 5 min. The Lotgering orientation factor of the (00l) peaks of Ti3SiC2 prepared under an MF was 0.96, and the relative density of samples exceeded 99%. The bending strength and fracture toughness of Ti3SiC2 were improved by texturing. The textured Ti3SiC2 exhibited an excellent bending strength of 978 MPa, but Al2O3 addition, reduced the bending strength and fracture toughness. The textured Ti3SiC2 showed the plastic deformation at a temperature of approximately 1173 K.

本文言語English
ページ(範囲)829-834
ページ数6
ジャーナルMaterials Transactions
59
5
DOI
出版ステータスPublished - 2018
外部発表はい

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Fabrication and mechanical properties of textured Ti<sub>3</sub>SiC<sub>2</sub> systems using commercial powder」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル