Fabrication of nickel dots using selective electroless deposition on silicon wafer

Tetsuya Osaka*, Nao Takano, Shinichi Komaba

*この研究の対応する著者

研究成果: Article査読

14 被引用数 (Scopus)

抄録

The selective deposition of nickel on n-Si(100) wafer in aqueous solution was investigated. It was confirmed by cross-sectional FE-TEM examination that the deposition of nickel occurred from a solution of nickel ions prepared by excluding the hypophosphitc reducing agent from the conventional electroless nickel plating bath, and that this deposition reaction accompanied the formation of SiO2. This finding shows that the electrons needed to reduce the nickel ions to the metal are supplied directly from the Si wafer. By utilizing this galvanic displacement reaction, nickel metal in the form of minute dots measuring 1 μm in diameter was selectively deposited using a silicon oxide layer as the resist in combination with a two-step process, which consisted of the first step of immersing a Si water into a solution containing nickel ions but no reducing agent to form nuclei of nickel metal, and the second step of immersing the wafer with the nuclei into a conventional electroless nickel plating bath to cause the growth of the nuclei to the desired size.

本文言語English
ページ(範囲)657-658
ページ数2
ジャーナルChemistry Letters
7
DOI
出版ステータスPublished - 1998 1 1

ASJC Scopus subject areas

  • 化学 (全般)

フィンガープリント

「Fabrication of nickel dots using selective electroless deposition on silicon wafer」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル