抄録
Super-plastic zirconia-dispersed alumina ceramics with fine-grained microstructure and the other is highly textured alumina were prepared. Colloidal processing was applied to obtain dense and homogeneous zirconia-dispersed alumina ceramics with mean grain size of 0.45 μm. Large tensile elongation exceeding 550% was achieved for 10 vol% zirconia-dispersed Al2O3 at 1773 K. High magnetic field (10T) was applied during slip casting of alumina suspension to produce textured microstructure. Green body with slight degree of crystallographic orientation was obtained and the degree of texture increased with increasing temperature. After densification, alumina grains grow to yield ceramics with textured grains and high degrees of crystallographic orientation. This processing can be applied to other ceramics with asymmetric unit cell.
| 本文言語 | English |
|---|---|
| ページ（範囲） | 619-622 |
| ページ数 | 4 |
| ジャーナル | Key Engineering Materials |
| 巻 | 224-226 |
| 出版ステータス | Published - 2002 1月 1 |
| 外部発表 | はい |
| イベント | Proceedings of the Second China International Conference on High-Performance Ceramics (CICC-2) - Kunming, China 継続期間: 2001 11月 11 → 2001 11月 15 |
ASJC Scopus subject areas
- 材料科学（全般）
- 材料力学
- 機械工学