Features of ferroelectric states in the simple-perovskite mixed-oxide system (1-x)Pb(Zn1/3Nb2/3)O3-xPbTiO3with lower Ti contents

Hirofumi Tsukasaki, Yuka Uneno, Shigeo Mori, Yasumasa Koyama

研究成果: Article査読

1 被引用数 (Scopus)

抄録

A mixed-oxide system (1 - x)Pb(Zn1/3Nb2/3)O3-xPbTiO3, which has a simple perovskite structure, has been reported to exhibit remarkable piezoelectric responses for 0 < x ≤ 0.08. To understand the ferroelectric states for 0 < x < 0.10, the crystallographic features of plate-shaped single crystals with various sample orientations have been examined by transmission electron microscopy. Owing to both the bending of specimens and the complicated nanometer-scale domain structures, it was difficult to obtain a contrast reversal due to the failure of Friedel's law. In some cases, however, it was possible to analyze the ferroelectric domain structures of the sample. Although the typical 109° domain structure of the ferroelectric rhombohedral state was found for x = 0.02, as a major feature in [110]c-oriented single crystals, the ferroelectric states for 0 < x ≤ 0.08 were found to be characterized by an assembly of nanometer-scale polar (NP) domains with rhombohedral symmetry. In [210]c-oriented crystals, on the other hand, the so-called MC state with monoclinic symmetry was present for x ≈ 0.08. Furthermore, on the basis of in-situ observation, the evolution of a mazepattern domain structure in the Mc state upon cooling from the paraelectric state occurs via a local flip-flop between two polarization vectors, which are nearly parallel to the 210c directions. It is likely that this behavior is directly associated with the ultrahigh piezoelectric deformations found for x ≈ 0.08.

本文言語English
論文番号034708
ジャーナルjournal of the physical society of japan
85
3
DOI
出版ステータスPublished - 2016

ASJC Scopus subject areas

  • Physics and Astronomy(all)

フィンガープリント 「Features of ferroelectric states in the simple-perovskite mixed-oxide system (1-x)Pb(Zn<sub>1/3</sub>Nb<sub>2/3</sub>)O<sub>3</sub>-xPbTiO<sub>3</sub>with lower Ti contents」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル